Oxford Polymers PPS-30GF-10PTFE-BK PPS, 30% Glass Fiber Reinforced, 10% PTFE

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer Oxford Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PPS-30GF-10PTFE-BK PPS, 30% Glass Fiber Reinforced, 10% PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (30% Reinforced), 10% PTFE, Polyphenylene sulfide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAppearance: BlackInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792
Water Absorption at Saturation 0.0200 %
0.0200 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00200 cm/cm

@Thickness 3.17 mm
0.00200 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 128 MPa
18500 psi
ASTM D638
Elongation at Break 1.50 %
1.50 %
ASTM D638
Flexural Strength 186 MPa
27000 psi
ASTM D790
Flexural Modulus 10.3 GPa
1500 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.17 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 10.8 µm/m-°C
6.00 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 293 - 321 °C
560 - 610 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature <= 121 °C
<= 250 °F
Dry Time 4.00 hour
4.00 hour