Oxford Polymers PEI 1010 PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer Oxford Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PEI 1010 PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: (Unreinforced), Polyetherimide injection molding grade, high flow Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristics: Colors AvailableInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
Water Absorption at Saturation 0.250 %
0.250 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
ASTM D638
Elongation at Break 3.00 %
3.00 %
ASTM D638
Flexural Strength 152 MPa
22000 psi
ASTM D790
Flexural Modulus 3.31 GPa
480 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 349 - 371 °C
660 - 700 °F
Middle Barrel Temperature 354 - 377 °C
670 - 710 °F
Front Barrel Temperature 360 - 382 °C
680 - 720 °F
Nozzle Temperature 360 - 382 °C
680 - 720 °F
Melt Temperature 338 - 427 °C
640 - 800 °F
Mold Temperature 65.6 - 177 °C
150 - 350 °F
Drying Temperature <= 135 °C
<= 275 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour