Oxford Polymers PC 30CF-925 Black PC, 30% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer Oxford Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PC 30CF-925 Black PC, 30% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (30% Reinforced), PBT injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristics: High Strength, electrically and thermally conductiveInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D792
Water Absorption at Saturation 0.120 %
0.120 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00200 cm/cm

@Thickness 3.17 mm
0.00200 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 152 MPa
22100 psi
ASTM D638
Elongation at Break 2.00 %
2.00 %
ASTM D638
Flexural Strength 245 MPa
35500 psi
ASTM D790
Flexural Modulus 13.8 GPa
2000 ksi
ASTM D790
Izod Impact, Notched 0.828 J/cm

@Thickness 3.17 mm
1.55 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 302 - 316 °C
575 - 600 °F
Middle Barrel Temperature 316 - 332 °C
600 - 630 °F
Front Barrel Temperature 310 - 327 °C
590 - 620 °F
Nozzle Temperature 310 - 327 °C
590 - 620 °F
Melt Temperature 304 - 327 °C
580 - 620 °F
Mold Temperature 71.1 - 87.8 °C
160 - 190 °F
Drying Temperature 121 °C
250 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour