Oxford Polymers Oxnilon 6-60GF(DRY) PA6, 60% Glass Fiber Reinforced, Dry

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer	Oxford Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Oxford Polymers Oxnilon 6-60GF(DRY) PA6, 60% Glass Fiber Reinforced, Dry.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Glass Fiber (60% Reinforced), Nylon 6 injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents, Lubricants and Heat Stabilizers Special Characteristics: Colors AvailableInformation provided by Oxford Polymers

Physical Properties	Metric	English	Comments
Density	1.65 g/cc	0.0596 lb/in³	ASTM D792
Water Absorption at Saturation	4.50 %	4.50 %	ASTM D570
Linear Mold Shrinkage, Flow	0.00200 cm/cm @Thickness 3.17 mm	0.00200 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	241 MPa	35000 psi	ASTM D638
Elongation at Break	1.00 %	1.00 %	ASTM D638
Flexural Strength	359 MPa	52000 psi	ASTM D790
Flexural Modulus	16.2 GPa	2350 ksi	ASTM D790
Izod Impact, Notched	2.14 J/cm @Thickness 3.17 mm	4.00 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	212 °C	414 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	260 - 288 °C	500 - 550 °F
Middle Barrel Temperature	271 - 299 °C	520 - 570 °F
Front Barrel Temperature	279 - 307 °C	535 - 585 °F
Nozzle Temperature	279 - 307 °C	535 - 585 °F
Melt Temperature	271 - 299 °C	520 - 570 °F
Mold Temperature	65.6 - 124 °C	150 - 255 °F
Drying Temperature	87.8 °C	190 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour