Overview of materials for Polypropylene with Carbon Black Filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Carbon Black Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene with Carbon Black Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Carbon Black Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.947 - 1.10 g/cc
0.0342 - 0.0397 lb/in³
Average value: 1.00 g/cc Grade Count:18
Water Absorption 0.0100 - 0.0300 %
0.0100 - 0.0300 %
Average value: 0.0167 % Grade Count:3
Thickness 102 microns
4.00 mil
Average value: 102 microns Grade Count:8
Linear Mold Shrinkage 0.0100 - 0.0200 cm/cm
0.0100 - 0.0200 in/in
Average value: 0.0146 cm/cm Grade Count:13
Melt Flow 0.400 - 35.0 g/10 min
0.400 - 35.0 g/10 min
Average value: 8.14 g/10 min Grade Count:9
Mechanical Properties Metric English Comments
Hardness, Shore A 96.0 - 99.0
96.0 - 99.0
Average value: 97.5 Grade Count:8
Hardness, Shore D 70.0 - 74.0
70.0 - 74.0
Average value: 72.3 Grade Count:8
Tensile Strength, Ultimate 16.5 - 32.0 MPa
2390 - 4640 psi
Average value: 23.4 MPa Grade Count:11
Tensile Strength, Yield 20.7 - 44.8 MPa
3000 - 6500 psi
Average value: 26.8 MPa Grade Count:7
Film Elongation at Break, MD 4.00 - 500 %
4.00 - 500 %
Average value: 252 % Grade Count:4
Elongation at Break 2.00 - 130 %
2.00 - 130 %
Average value: 23.0 % Grade Count:13
Elongation at Yield 7.00 - 12.0 %
7.00 - 12.0 %
Average value: 9.28 % Grade Count:5
Modulus of Elasticity 0.483 - 2.20 GPa
70.1 - 319 ksi
Average value: 1.31 GPa Grade Count:3
Flexural Yield Strength 20.7 - 48.0 MPa
3000 - 6960 psi
Average value: 30.0 MPa Grade Count:7
Flexural Modulus 0.965 - 3.10 GPa
140 - 450 ksi
Average value: 1.67 GPa Grade Count:17
Izod Impact, Notched 0.502 - 8.33 J/cm
0.940 - 15.6 ft-lb/in
Average value: 3.63 J/cm Grade Count:7
Izod Impact, Unnotched 1.00 J/cm - NB
1.87 ft-lb/in - NB
Average value: 7.43 J/cm Grade Count:7
Izod Impact, Notched (ISO) 1.50 kJ/m² - NB
0.714 ft-lb/in² - NB
Average value: 27.7 kJ/m² Grade Count:10
1.20 kJ/m² - NB

@Temperature -20.0 - -20.0 °C
0.571 ft-lb/in² - NB

@Temperature -4.00 - -4.00 °F
Average value: 5.84 kJ/m² Grade Count:7
1.20 kJ/m² - NB

@Thickness 4.00 - 4.00 mm
0.571 ft-lb/in² - NB

@Thickness 0.157 - 0.157 in
Average value: 5.84 kJ/m² Grade Count:7
Izod Impact, Unnotched (ISO) 16.0 kJ/m² - NB
7.61 ft-lb/in² - NB
Average value: 48.7 kJ/m² Grade Count:10
9.00 kJ/m² - NB

@Temperature -20.0 - -20.0 °C
4.28 ft-lb/in² - NB

@Temperature -4.00 - -4.00 °F
Average value: 17.7 kJ/m² Grade Count:7
9.00 kJ/m² - NB

@Thickness 4.00 - 4.00 mm
4.28 ft-lb/in² - NB

@Thickness 0.157 - 0.157 in
Average value: 17.7 kJ/m² Grade Count:7
Charpy Impact Unnotched 1.40 - 1000 J/cm²
6.66 - 4760 ft-lb/in²
Average value: 1.40 J/cm² Grade Count:8
0.500 - 999.9 J/cm²

@Temperature -20.0 - -20.0 °C
2.38 - 4759 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.500 J/cm² Grade Count:7
0.500 - 999.9 J/cm²

@Thickness 102 - 102 mm
2.38 - 4759 ft-lb/in²

@Thickness 4.00 - 4.00 in
Average value: 0.500 J/cm² Grade Count:7
Charpy Impact, Notched 0.300 - 5.00 J/cm²
1.43 - 23.8 ft-lb/in²
Average value: 2.44 J/cm² Grade Count:8
0.200 - 2.60 J/cm²

@Temperature -20.0 - -20.0 °C
0.952 - 12.4 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 1.39 J/cm² Grade Count:7
0.200 - 2.60 J/cm²

@Thickness 102 - 102 mm
0.952 - 12.4 ft-lb/in²

@Thickness 4.00 - 4.00 in
Average value: 1.39 J/cm² Grade Count:7
Film Tensile Strength at Break, MD 25.0 - 33.0 MPa
3630 - 4790 psi
Average value: 28.3 MPa Grade Count:4
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 107 - 300 °C
225 - 572 °F
Average value: 185 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 74.0 - 149 °C
165 - 300 °F
Average value: 99.8 °C Grade Count:12
Deflection Temperature at 1.8 MPa (264 psi) 46.0 - 71.0 °C
115 - 160 °F
Average value: 55.8 °C Grade Count:13
Vicat Softening Point 80.0 - 156 °C
176 - 313 °F
Average value: 134 °C Grade Count:8
Electrical Properties Metric English Comments
Electrical Resistivity 5.00 - 1.00e+9 ohm-cm
5.00 - 1.00e+9 ohm-cm
Average value: 7.19e+7 ohm-cm Grade Count:15
Surface Resistance 10.0 - 1.00e+9 ohm
10.0 - 1.00e+9 ohm
Average value: 6.72e+7 ohm Grade Count:17
Processing Properties Metric English Comments
Melt Temperature 200 - 270 °C
392 - 518 °F
Average value: 229 °C Grade Count:11
Mold Temperature 32.2 - 80.0 °C
90.0 - 176 °F
Average value: 58.9 °C Grade Count:7
Roll Temperature 60.0 - 100 °C
140 - 212 °F
Average value: 80.7 °C Grade Count:5
Drying Temperature 60.0 - 82.2 °C
140 - 180 °F
Average value: 72.4 °C Grade Count:10
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Average value: 70.0 MPa Grade Count:4