Overview of materials for Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.08 - 1.62 g/cc
0.0390 - 0.0585 lb/in³
Average value: 1.48 g/cc Grade Count:18
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 29.4 % Grade Count:8
Water Absorption 0.0200 - 0.0300 %
0.0200 - 0.0300 %
Average value: 0.0233 % Grade Count:9
Linear Mold Shrinkage 0.000100 - 0.00400 cm/cm
0.000100 - 0.00400 in/in
Average value: 0.00150 cm/cm Grade Count:17
Linear Mold Shrinkage, Transverse 0.00250 - 0.00500 cm/cm
0.00250 - 0.00500 in/in
Average value: 0.00387 cm/cm Grade Count:4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 119 - 172 MPa
17300 - 25000 psi
Average value: 148 MPa Grade Count:18
Elongation at Break 0.000 - 2.00 %
0.000 - 2.00 %
Average value: 1.13 % Grade Count:18
Modulus of Elasticity 11.0 - 34.5 GPa
1600 - 5000 ksi
Average value: 23.1 GPa Grade Count:14
Flexural Yield Strength 148 - 262 MPa
21500 - 38000 psi
Average value: 219 MPa Grade Count:16
Flexural Modulus 9.65 - 27.6 GPa
1400 - 4000 ksi
Average value: 19.4 GPa Grade Count:17
Izod Impact, Notched 0.374 - 0.641 J/cm
0.700 - 1.20 ft-lb/in
Average value: 0.487 J/cm Grade Count:17
Izod Impact, Unnotched 2.08 - 4.43 J/cm
3.90 - 8.30 ft-lb/in
Average value: 2.97 J/cm Grade Count:13
Izod Impact, Notched (ISO) 5.70 - 8.00 kJ/m²
2.71 - 3.81 ft-lb/in²
Average value: 6.67 kJ/m² Grade Count:3
Izod Impact, Unnotched (ISO) 24.2 - 31.0 kJ/m²
11.5 - 14.8 ft-lb/in²
Average value: 27.8 kJ/m² Grade Count:3
Falling Dart Impact 4.50 - 15.1 J
3.32 - 11.1 ft-lb
Average value: 8.17 J Grade Count:3
Coefficient of Friction 0.140 - 0.390
0.140 - 0.390
Average value: 0.292 Grade Count:5
Coefficient of Friction, Static 0.180 - 0.340
0.180 - 0.340
Average value: 0.280 Grade Count:5
K (wear) Factor 8.00 - 94.7 x 10-8 mm³/N-M
3.97 - 47.0 x 10-10 in³-min/ft-lb-hr
Average value: 36.0 x 10<sup>-8</sup> mm³/N-M Grade Count:5
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 - 280 °C
500 - 536 °F
Average value: 268 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 249 - 270 °C
480 - 518 °F
Average value: 262 °C Grade Count:18
Flammability, UL94 V-0
V-0
Grade Count:8
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 - 1.00e+6 ohm-cm
1.00 - 1.00e+6 ohm-cm
Average value: 143000 ohm-cm Grade Count:10
Processing Properties Metric English Comments
Processing Temperature 288 - 321 °C
550 - 610 °F
Average value: 304 °C Grade Count:7
Melt Temperature 290 - 329 °C
554 - 625 °F
Average value: 314 °C Grade Count:9
Mold Temperature 130 - 177 °C
266 - 350 °F
Average value: 152 °C Grade Count:16
Drying Temperature 121 - 150 °C
250 - 302 °F
Average value: 140 °C Grade Count:8
Injection Pressure 41.4 - 103 MPa
6000 - 15000 psi
Average value: 83.6 MPa Grade Count:10