Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, NCG Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, NCG Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.18 - 1.42 g/cc
0.0426 - 0.0513 lb/in³
Average value: 1.32 g/cc Grade Count:27
Filler Content 5.00 - 20.0 %
5.00 - 20.0 %
Average value: 12.6 % Grade Count:21
Water Absorption 0.100 - 0.200 %
0.100 - 0.200 %
Average value: 0.106 % Grade Count:18
Additive Loading 15.0 - 40.0 %
15.0 - 40.0 %
Average value: 26.3 % Grade Count:4
Linear Mold Shrinkage 0.000500 - 0.00600 cm/cm
0.000500 - 0.00600 in/in
Average value: 0.00180 cm/cm Grade Count:27
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 62.1 - 152 MPa
9000 - 22000 psi
Average value: 98.7 MPa Grade Count:27
Elongation at Break 0.500 - 5.00 %
0.500 - 5.00 %
Average value: 1.77 % Grade Count:27
Modulus of Elasticity 4.48 - 14.5 GPa
650 - 2100 ksi
Average value: 8.91 GPa Grade Count:27
Flexural Yield Strength 110 - 193 MPa
16000 - 28000 psi
Average value: 142 MPa Grade Count:27
Flexural Modulus 4.14 - 13.8 GPa
600 - 2000 ksi
Average value: 8.00 GPa Grade Count:27
Izod Impact, Notched 0.374 - 1.33 J/cm
0.700 - 2.50 ft-lb/in
Average value: 0.655 J/cm Grade Count:27
Izod Impact, Unnotched 2.14 - 5.34 J/cm
4.00 - 10.0 ft-lb/in
Average value: 3.01 J/cm Grade Count:26
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 98.9 - 146 °C
210 - 295 °F
Average value: 108 °C Grade Count:22
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:22
Electrical Properties Metric English Comments
Electrical Resistivity 0.100 - 1000 ohm-cm
0.100 - 1000 ohm-cm
Average value: 258 ohm-cm Grade Count:27
Surface Resistance 1.00 - 1.00e+6 ohm
1.00 - 1.00e+6 ohm
Average value: 252000 ohm Grade Count:27
Static Decay 0.500 - 2.00 sec
0.500 - 2.00 sec
Average value: 1.77 sec Grade Count:26
Processing Properties Metric English Comments
Processing Temperature 232 - 266 °C
450 - 510 °F
Average value: 249 °C Grade Count:21
Melt Temperature 232 - 274 °C
450 - 525 °F
Average value: 257 °C Grade Count:6
Mold Temperature 51.7 - 93.3 °C
125 - 200 °F
Average value: 73.0 °C Grade Count:27
Drying Temperature 79.0 - 93.3 °C
174 - 200 °F
Average value: 92.1 °C Grade Count:6
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:5
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:5
Injection Pressure 6.89 - 103 MPa
1000 - 15000 psi
Average value: 85.0 MPa Grade Count:26