Overview of materials for Polycarbonate, Glass Fiber & Bead Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber & Bead Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate, Glass Fiber & Bead Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber & Bead Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.26 - 1.42 g/cc
0.0455 - 0.0515 lb/in³
Average value: 1.31 g/cc Grade Count:7
Water Absorption 0.160 - 0.200 %
0.160 - 0.200 %
Average value: 0.187 % Grade Count:3
Linear Mold Shrinkage 0.00200 - 0.00600 cm/cm
0.00200 - 0.00600 in/in
Average value: 0.00386 cm/cm Grade Count:7
Melt Flow 9.00 - 15.0 g/10 min
9.00 - 15.0 g/10 min
Average value: 12.0 g/10 min Grade Count:4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 53.4 - 86.0 MPa
7750 - 12500 psi
Average value: 66.8 MPa Grade Count:5
Elongation at Break 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 2.40 % Grade Count:5
Modulus of Elasticity 3.80 - 5.20 GPa
551 - 754 ksi
Average value: 4.73 GPa Grade Count:3
Flexural Yield Strength 86.2 - 132 MPa
12500 - 19100 psi
Average value: 105 MPa Grade Count:7
Flexural Modulus 2.41 - 5.40 GPa
350 - 783 ksi
Average value: 4.26 GPa Grade Count:7
Izod Impact, Notched 0.530 - 1.60 J/cm
0.993 - 3.00 ft-lb/in
Average value: 1.08 J/cm Grade Count:7
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 - 149 °C
225 - 300 °F
Average value: 132 °C Grade Count:6
Processing Properties Metric English Comments
Melt Temperature 260 - 316 °C
500 - 601 °F
Average value: 284 °C Grade Count:9
Mold Temperature 77.0 - 121 °C
171 - 250 °F
Average value: 104 °C Grade Count:9
Drying Temperature 121 °C
250 °F
Average value: 121 °C Grade Count:3