Overview of materials for Nylon 66, Extruded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, Extruded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Extruded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.14 - 1.37 g/cc
0.0412 - 0.0495 lb/in³
Average value: 1.17 g/cc Grade Count:14
Water Absorption 0.300 - 8.50 %
0.300 - 8.50 %
Average value: 2.63 % Grade Count:9
Moisture Absorption at Equilibrium 2.40 - 2.70 %
2.40 - 2.70 %
Average value: 2.53 % Grade Count:4
Water Absorption at Saturation 2.50 - 8.50 %
2.50 - 8.50 %
Average value: 7.04 % Grade Count:9
Linear Mold Shrinkage 0.00500 - 0.0200 cm/cm
0.00500 - 0.0200 in/in
Average value: 0.0124 cm/cm Grade Count:7
Mechanical Properties Metric English Comments
Hardness, Rockwell M 79.0 - 101
79.0 - 101
Average value: 88.3 Grade Count:4
Hardness, Rockwell R 115 - 120
115 - 120
Average value: 117 Grade Count:6
Hardness, Shore D 80.0 - 82.0
80.0 - 82.0
Average value: 80.7 Grade Count:3
Tensile Strength, Ultimate 82.7 - 138 MPa
12000 - 20000 psi
Average value: 95.9 MPa Grade Count:6
Tensile Strength, Yield 83.0 - 179 MPa
12000 - 26000 psi
Average value: 101 MPa Grade Count:6
Elongation at Break 3.00 - 90.0 %
3.00 - 90.0 %
Average value: 45.6 % Grade Count:11
Modulus of Elasticity 2.80 - 3.70 GPa
406 - 537 ksi
Average value: 3.20 GPa Grade Count:5
Flexural Yield Strength 100 - 269 MPa
14500 - 39000 psi
Average value: 141 MPa Grade Count:10
Flexural Modulus 2.60 - 9.65 GPa
377 - 1400 ksi
Average value: 3.97 GPa Grade Count:12
Compressive Yield Strength 32.0 - 100 MPa
4640 - 14500 psi
Average value: 74.0 MPa Grade Count:3
Izod Impact, Notched 0.320 - 1.12 J/cm
0.600 - 2.10 ft-lb/in
Average value: 0.767 J/cm Grade Count:8
Izod Impact, Notched (ISO) 5.00 - 5.70 kJ/m²
2.38 - 2.71 ft-lb/in²
Average value: 5.23 kJ/m² Grade Count:3
3.00 - 4.00 kJ/m²

@Temperature -40.0 - -20.0 °C
1.43 - 1.90 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.50 kJ/m² Grade Count:1
Coefficient of Friction 0.250 - 0.600
0.250 - 0.600
Average value: 0.333 Grade Count:3
Limiting Pressure Velocity 0.0800 - 0.130 MPa-m/sec
2280 - 3710 psi-ft/min
Average value: 0.101 MPa-m/sec Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 10.0 - 100 µm/m-°C
5.56 - 55.6 µin/in-°F
Average value: 63.3 µm/m-°C Grade Count:8
90.0 - 90.0 µm/m-°C

@Temperature 93.3 - 238 °C
50.0 - 50.0 µin/in-°F

@Temperature 200 - 460 °F
Average value: 90.0 µm/m-°C Grade Count:1
Thermal Conductivity 0.230 - 0.280 W/m-K
1.60 - 1.94 BTU-in/hr-ft²-°F
Average value: 0.252 W/m-K Grade Count:3
Melting Point 254 - 265 °C
489 - 509 °F
Average value: 258 °C Grade Count:8
Maximum Service Temperature, Air 80.0 - 241 °C
176 - 466 °F
Average value: 130 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 200 - 259 °C
392 - 499 °F
Average value: 230 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 70.0 - 256 °C
158 - 492 °F
Average value: 119 °C Grade Count:12
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+11 - 1.00e+15 ohm-cm
1.00e+11 - 1.00e+15 ohm-cm
Average value: 6.50e+14 ohm-cm Grade Count:8
Surface Resistance 1.00e+12 - 1.00e+13 ohm
1.00e+12 - 1.00e+13 ohm
Average value: 7.00e+12 ohm Grade Count:3
Dielectric Constant 3.50 - 4.30
3.50 - 4.30
Average value: 3.76 Grade Count:6
Dielectric Strength 11.8 - 30.5 kV/mm
300 - 775 kV/in
Average value: 22.6 kV/mm Grade Count:8
Dissipation Factor 0.0130 - 0.0240
0.0130 - 0.0240
Average value: 0.0190 Grade Count:3
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 250 - 304 °C
482 - 580 °F
Average value: 276 °C Grade Count:3