Overview of materials for Nylon 46, Unreinforced

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 46, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.10 - 1.43 g/cc
0.0397 - 0.0517 lb/in³
Average value: 1.21 g/cc Grade Count:40
Water Absorption 0.600 - 13.5 %
0.600 - 13.5 %
Average value: 8.91 % Grade Count:17
Moisture Absorption at Equilibrium 2.00 - 3.70 %
2.00 - 3.70 %
Average value: 3.26 % Grade Count:24
Water Absorption at Saturation 7.00 - 14.0 %
7.00 - 14.0 %
Average value: 10.0 % Grade Count:4
Viscosity Test 175 - 220 cm³/g
175 - 220 cm³/g
Average value: 187 cm³/g Grade Count:7
Linear Mold Shrinkage 0.00330 - 0.0200 cm/cm
0.00330 - 0.0200 in/in
Average value: 0.0188 cm/cm Grade Count:24
Linear Mold Shrinkage, Transverse 0.0150 - 0.0200 cm/cm
0.0150 - 0.0200 in/in
Average value: 0.0195 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92.0 - 97.0
92.0 - 97.0
Average value: 93.7 Grade Count:3
Hardness, Rockwell R 90.0 - 100
90.0 - 100
Average value: 95.0 Grade Count:4
Ball Indentation Hardness 165 - 200 MPa
23900 - 29000 psi
Average value: 172 MPa Grade Count:3
Tensile Strength, Ultimate 65.0 - 197 MPa
9430 - 28500 psi
Average value: 107 MPa Grade Count:5
Tensile Strength, Yield 45.0 - 105 MPa
6530 - 15200 psi
Average value: 72.6 MPa Grade Count:33
30.0 - 50.0 MPa

@Temperature 120 - 200 °C
4350 - 7250 psi

@Temperature 248 - 392 °F
Average value: 38.8 MPa Grade Count:2
Elongation at Break 2.80 - 280 %
2.80 - 280 %
Average value: 44.8 % Grade Count:28
>= 50.0 %

@Temperature 120 - 200 °C
>= 50.0 %

@Temperature 248 - 392 °F
Average value: 50.0 % Grade Count:2
Elongation at Yield 5.00 - 55.0 %
5.00 - 55.0 %
Average value: 27.7 % Grade Count:25
Modulus of Elasticity 0.600 - 12.1 GPa
87.0 - 1750 ksi
Average value: 2.43 GPa Grade Count:36
0.500 - 0.800 GPa

@Temperature 120 - 200 °C
72.5 - 116 ksi

@Temperature 248 - 392 °F
Average value: 0.637 GPa Grade Count:2
Flexural Yield Strength 103 - 283 MPa
15000 - 41000 psi
Average value: 135 MPa Grade Count:8
Flexural Modulus 0.900 - 11.4 GPa
131 - 1650 ksi
Average value: 3.28 GPa Grade Count:12
0.600 - 0.800 GPa

@Temperature 120 - 160 °C
87.0 - 116 ksi

@Temperature 248 - 320 °F
Average value: 0.700 GPa Grade Count:2
Compressive Yield Strength 23.0 - 110 MPa
3340 - 16000 psi
Average value: 66.5 MPa Grade Count:3
Izod Impact, Notched 0.320 - 0.801 J/cm
0.600 - 1.50 ft-lb/in
Average value: 0.686 J/cm Grade Count:7
0.74746 - 0.74746 J/cm

@Temperature -40.0 - -40.0 °C
1.4003 - 1.4003 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.747 J/cm Grade Count:2
0.74746 - 0.74746 J/cm

@Thickness 3.17 - 3.17 mm
1.4003 - 1.4003 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 0.747 J/cm Grade Count:2
Izod Impact, Unnotched 4.27 - 5340 J/cm
8.00 - 10000 ft-lb/in
Average value: 8.81 J/cm Grade Count:4
Izod Impact, Notched (ISO) 8.00 - 35.0 kJ/m²
3.81 - 16.7 ft-lb/in²
Average value: 18.7 kJ/m² Grade Count:3
4.00 - 5.00 kJ/m²

@Temperature -40.0 - -40.0 °C
1.90 - 2.38 ft-lb/in²

@Temperature -40.0 - -40.0 °F
Average value: 4.33 kJ/m² Grade Count:3
Charpy Impact Unnotched 8.50 J/cm² - NB
40.5 ft-lb/in² - NB
Average value: 9.25 J/cm² Grade Count:25
8.50 J/cm² - NB

@Temperature -30.0 - -30.0 °C
40.5 ft-lb/in² - NB

@Temperature -22.0 - -22.0 °F
Average value: 10.1 J/cm² Grade Count:23
Charpy Impact, Notched 0.400 - 1000 J/cm²
1.90 - 4760 ft-lb/in²
Average value: 3.09 J/cm² Grade Count:31
0.300 - 3.00 J/cm²

@Temperature -30.0 - -30.0 °C
1.43 - 14.3 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.10 J/cm² Grade Count:24
Coefficient of Friction 0.200 - 0.600
0.200 - 0.600
Average value: 0.388 Grade Count:3
Tensile Creep Modulus, 1000 hours 500 - 850 MPa
72500 - 123000 psi
Average value: 570 MPa Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 72.0 - 160 µm/m-°C
40.0 - 88.9 µin/in-°F
Average value: 88.1 µm/m-°C Grade Count:26
CTE, linear, Transverse to Flow 90.0 - 180 µm/m-°C
50.0 - 100 µin/in-°F
Average value: 109 µm/m-°C Grade Count:17
Thermal Conductivity 0.300 - 0.303 W/m-K
2.08 - 2.10 BTU-in/hr-ft²-°F
Average value: 0.301 W/m-K Grade Count:3
Melting Point 290 - 295 °C
554 - 563 °F
Average value: 295 °C Grade Count:34
Maximum Service Temperature, Air 128 - 280 °C
262 - 536 °F
Average value: 162 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 200 - 290 °C
392 - 554 °F
Average value: 261 °C Grade Count:11
Deflection Temperature at 1.8 MPa (264 psi) 90.0 - 285 °C
194 - 545 °F
Average value: 176 °C Grade Count:26
Vicat Softening Point 250 - 290 °C
482 - 554 °F
Average value: 283 °C Grade Count:7
Glass Transition Temp, Tg 75.0 - 80.0 °C
167 - 176 °F
Average value: 75.6 °C Grade Count:9
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:20
Oxygen Index 24.0 - 29.0 %
24.0 - 29.0 %
Average value: 26.8 % Grade Count:5
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+15 ohm-cm
1000 - 1.00e+15 ohm-cm
Average value: 2.65e+14 ohm-cm Grade Count:32
Surface Resistance 1.00e+6 - 1.00e+14 ohm
1.00e+6 - 1.00e+14 ohm
Average value: 1.71e+13 ohm Grade Count:9
Dielectric Constant 3.20 - 22.0
3.20 - 22.0
Average value: 6.65 Grade Count:11
Dielectric Strength 15.0 - 30.0 kV/mm
381 - 762 kV/in
Average value: 21.6 kV/mm Grade Count:26
Dissipation Factor 0.000500 - 0.0870
0.000500 - 0.0870
Average value: 0.0194 Grade Count:9
Comparative Tracking Index 325 - 600 V
325 - 600 V
Average value: 444 V Grade Count:24