Overview of materials for Epoxy, Encapsulating, Glass or Mineral Filled

Category Polymer , Thermoset , Epoxy , Epoxy, Encapsulating, Glass or Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Epoxy, Encapsulating, Glass or Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Glass or Mineral Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.70 - 2.00 g/cc
0.0614 - 0.0723 lb/in³
Average value: 1.86 g/cc Grade Count:14
Apparent Bulk Density 0.740 - 0.800 g/cc
0.0267 - 0.0289 lb/in³
Average value: 0.770 g/cc Grade Count:4
Water Absorption 0.100 - 0.250 %
0.100 - 0.250 %
Average value: 0.197 % Grade Count:6
0.110 - 0.300 %

@Temperature 50.0 - 50.0 °C
0.110 - 0.300 %

@Temperature 122 - 122 °F
Average value: 0.202 % Grade Count:5
0.110 - 0.300 %

@Time 173000 - 173000 sec
0.110 - 0.300 %

@Time 48.0 - 48.0 hour
Average value: 0.202 % Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00367 cm/cm Grade Count:12
Mechanical Properties Metric English Comments
Hardness, Barcol 60.0 - 70.0
60.0 - 70.0
Average value: 65.9 Grade Count:7
Tensile Strength, Ultimate 41.0 - 107 MPa
5950 - 15500 psi
Average value: 77.7 MPa Grade Count:13
Flexural Yield Strength 83.0 - 150 MPa
12000 - 21800 psi
Average value: 117 MPa Grade Count:13
Flexural Modulus 11.7 - 19.0 GPa
1700 - 2760 ksi
Average value: 14.6 GPa Grade Count:12
Compressive Yield Strength 172 - 379 MPa
25000 - 55000 psi
Average value: 234 MPa Grade Count:13
Izod Impact, Notched 0.160 - 0.370 J/cm
0.300 - 0.693 ft-lb/in
Average value: 0.282 J/cm Grade Count:12
Thermal Properties Metric English Comments
CTE, linear 12.6 - 32.0 µm/m-°C
7.00 - 17.8 µin/in-°F
Average value: 22.6 µm/m-°C Grade Count:12
CTE, linear, Transverse to Flow 26.4 - 80.0 µm/m-°C
14.7 - 44.4 µin/in-°F
Average value: 58.5 µm/m-°C Grade Count:7
Thermal Conductivity 0.259 - 1.26 W/m-K
1.80 - 8.72 BTU-in/hr-ft²-°F
Average value: 0.795 W/m-K Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 165 - 282 °C
329 - 540 °F
Average value: 229 °C Grade Count:10
Glass Transition Temp, Tg 110 - 165 °C
230 - 329 °F
Average value: 151 °C Grade Count:5
Flammability, UL94 V-0
V-0
Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Average value: 1.00e+15 ohm-cm Grade Count:4
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
Average value: 1.00e+15 ohm Grade Count:4
Dielectric Constant 3.00 - 4.80
3.00 - 4.80
Average value: 4.03 Grade Count:13
Dielectric Strength 12.8 - 17.0 kV/mm
325 - 432 kV/in
Average value: 14.0 kV/mm Grade Count:13
Dissipation Factor 0.00400 - 0.0200
0.00400 - 0.0200
Average value: 0.0131 Grade Count:13
Arc Resistance 178 - 190 sec
178 - 190 sec
Average value: 181 sec Grade Count:12
Processing Properties Metric English Comments
Processing Temperature 150 - 193 °C
302 - 379 °F
Average value: 166 °C Grade Count:5