Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.04 - 1.33 g/cc
0.0376 - 0.0480 lb/in³
Average value: 1.18 g/cc Grade Count:142
Water Absorption 0.0300 - 0.300 %
0.0300 - 0.300 %
Average value: 0.274 % Grade Count:26
Water Absorption at Saturation 0.300 - 1.00 %
0.300 - 1.00 %
Average value: 0.650 % Grade Count:4
Viscosity 350000 - 350000 cP

@Temperature 200 - 200 °C
350000 - 350000 cP

@Temperature 392 - 392 °F
Average value: 223000 cP Grade Count:1
159300 - 159300 cP

@Temperature 191 - 191 °C
159300 - 159300 cP

@Temperature 375 - 375 °F
Average value: 223000 cP Grade Count:1
159300 - 159300 cP

@Shear Rate 3000 - 3000 1/s
159300 - 159300 cP

@Shear Rate 3000 - 3000 1/s
Average value: 223000 cP Grade Count:1
Linear Mold Shrinkage 0.00200 - 0.00900 cm/cm
0.00200 - 0.00900 in/in
Average value: 0.00508 cm/cm Grade Count:111
Melt Flow 0.300 - 80.0 g/10 min
0.300 - 80.0 g/10 min
Average value: 17.1 g/10 min Grade Count:130
Mechanical Properties Metric English Comments
Hardness, Rockwell R 79.0 - 115
79.0 - 115
Average value: 101 Grade Count:91
Ball Indentation Hardness 75.0 - 82.0 MPa
10900 - 11900 psi
Average value: 79.3 MPa Grade Count:7
Tensile Strength, Ultimate 26.5 - 45.0 MPa
3840 - 6530 psi
Average value: 35.7 MPa Grade Count:63
8.00 - 15.0 MPa

@Temperature 60.0 - 90.0 °C
1160 - 2180 psi

@Temperature 140 - 194 °F
Average value: 11.5 MPa Grade Count:1
Tensile Strength, Yield 28.3 - 53.9 MPa
4100 - 7820 psi
Average value: 40.4 MPa Grade Count:114
Elongation at Break 3.00 - 56.0 %
3.00 - 56.0 %
Average value: 15.0 % Grade Count:91
50.0 - 95.0 %

@Temperature 60.0 - 90.0 °C
50.0 - 95.0 %

@Temperature 140 - 194 °F
Average value: 72.5 % Grade Count:1
Elongation at Yield 2.00 - 15.0 %
2.00 - 15.0 %
Average value: 4.20 % Grade Count:19
2.30 - 2.30 %

@Temperature 60.0 - 90.0 °C
2.30 - 2.30 %

@Temperature 140 - 194 °F
Average value: 2.30 % Grade Count:1
Modulus of Elasticity 1.47 - 2.70 GPa
213 - 392 ksi
Average value: 2.24 GPa Grade Count:44
1.50 - 1.90 GPa

@Temperature 60.0 - 90.0 °C
218 - 276 ksi

@Temperature 140 - 194 °F
Average value: 1.70 GPa Grade Count:1
Flexural Yield Strength 41.4 - 81.4 MPa
6000 - 11800 psi
Average value: 63.3 MPa Grade Count:108
Flexural Modulus 1.57 - 20.0 GPa
228 - 2900 ksi
Average value: 2.34 GPa Grade Count:134
Izod Impact, Notched 0.100 - 4.48 J/cm
0.187 - 8.40 ft-lb/in
Average value: 1.87 J/cm Grade Count:125
0.600 - 1.80 J/cm

@Temperature -20.0 - 0.000 °C
1.12 - 3.37 ft-lb/in

@Temperature -4.00 - 32.0 °F
Average value: 1.11 J/cm Grade Count:12
0.69407 - 1.81526 J/cm

@Temperature -40.0 - 0.000 °C
1.3003 - 3.40073 ft-lb/in

@Temperature -40.0 - 32.0 °F
Average value: 1.11 J/cm Grade Count:4
0.69407 - 1.81526 J/cm

@Thickness 3.17 - 3.20 mm
1.3003 - 3.40073 ft-lb/in

@Thickness 0.125 - 0.126 in
Average value: 1.11 J/cm Grade Count:4
Izod Impact, Unnotched 6.41 - 13.9 J/cm
12.0 - 26.0 ft-lb/in
Average value: 10.4 J/cm Grade Count:5
Izod Impact, Notched (ISO) 9.00 - 28.0 kJ/m²
4.28 - 13.3 ft-lb/in²
Average value: 16.6 kJ/m² Grade Count:18
3.00 - 14.0 kJ/m²

@Temperature -30.0 - -30.0 °C
1.43 - 6.66 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 7.45 kJ/m² Grade Count:8
Izod Impact, Unnotched (ISO) 70.0 kJ/m² - NB
33.3 ft-lb/in² - NB
Average value: 70.0 kJ/m² Grade Count:9
40.0 - 55.0 kJ/m²

@Temperature -30.0 - -30.0 °C
19.0 - 26.2 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 47.5 kJ/m² Grade Count:2
Charpy Impact Unnotched 5.00 J/cm² - NB
23.8 ft-lb/in² - NB
Average value: 6.17 J/cm² Grade Count:13
0.250 - 7.50 J/cm²

@Temperature -30.0 - -20.0 °C
1.19 - 35.7 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 4.47 J/cm² Grade Count:6
Charpy Impact, Notched 0.500 - 3.00 J/cm²
2.38 - 14.3 ft-lb/in²
Average value: 1.62 J/cm² Grade Count:19
0.300 - 1.30 J/cm²

@Temperature -30.0 - -20.0 °C
1.43 - 6.19 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.744 J/cm² Grade Count:9
Gardner Impact 2.71 - 36.2 J
2.00 - 26.7 ft-lb
Average value: 18.2 J Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 72.0 - 144 µm/m-°C
40.0 - 80.0 µin/in-°F
Average value: 94.5 µm/m-°C Grade Count:17
CTE, linear, Transverse to Flow 80.0 - 96.0 µm/m-°C
44.4 - 53.3 µin/in-°F
Average value: 86.1 µm/m-°C Grade Count:4
Thermal Conductivity 0.173 - 0.200 W/m-K
1.20 - 1.39 BTU-in/hr-ft²-°F
Average value: 0.187 W/m-K Grade Count:4
Hot Ball Pressure Test 80.0 - 105 °C
176 - 221 °F
Average value: 95.0 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 77.2 - 107 °C
171 - 225 °F
Average value: 89.5 °C Grade Count:55
Deflection Temperature at 1.8 MPa (264 psi) 66.1 - 196 °C
151 - 385 °F
Average value: 87.9 °C Grade Count:119
Vicat Softening Point 42.0 - 123 °C
108 - 253 °F
Average value: 93.7 °C Grade Count:101
Electrical Properties Metric English Comments
Electrical Resistivity 1e+05 - 1.00e+16 ohm-cm
1e+05 - 1.00e+16 ohm-cm
Average value: 1.65e+15 ohm-cm Grade Count:27
Surface Resistance 1e+05 - 1.00e+15 ohm
1e+05 - 1.00e+15 ohm
Average value: 5.86e+14 ohm Grade Count:8
Dielectric Constant 2.40 - 3.10
2.40 - 3.10
Average value: 2.89 Grade Count:7
Dielectric Strength 17.0 - 42.0 kV/mm
432 - 1070 kV/in
Average value: 26.4 kV/mm Grade Count:16
Dissipation Factor 0.00400 - 0.0125
0.00400 - 0.0125
Average value: 0.00795 Grade Count:7
Arc Resistance 60.0 - 120 sec
60.0 - 120 sec
Average value: 81.4 sec Grade Count:7
Comparative Tracking Index 250 - 600 V
250 - 600 V
Average value: 464 V Grade Count:16
Hot Wire Ignition, HWI 7.00 - 120 sec
7.00 - 120 sec
Average value: 33.6 sec Grade Count:9
High Amp Arc Ignition, HAI 60.0 - 199 arcs
60.0 - 199 arcs
Average value: 134 arcs Grade Count:9
High Voltage Arc-Tracking Rate, HVTR 10.0 - 150 mm/min
0.394 - 5.91 in/min
Average value: 102 mm/min Grade Count:9