Omnia Plastica PVDF Kynar

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer Omnia Plastica s.p.a.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Omnia Plastica PVDF Kynar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PVDF is a relatively new fluoropolymer. Like the other fluoropolymers, its best feature is its chemical resistance. The mechanical features of PVDF are notably higher than PTFE and it does not suffer strain under load.Features:Chemical: it has the typical high chemical properties of the fluoropolymers.Mechanical: compared to PTFE it has higher mechanical features, such as tensile stress and compressive strength.Very good resistance to low and high temperatures up to 150° C. as well as UV. ray resistance.Excellent dimensional stability.Low flammabilityLow friction coefficientColour: naturalWeak Point:Compared to PTFE the resistance to high temperature is lower (150 °C).Application:Chemical: the excellent chemical resistance to acids and alkali is typical of the fluoropolymers. It is used for components in the petrochemical and chemical industries.Food contact: physiologically inert, it is approved for food contact by the most important international standards organisations. Thanks to this feature, it is widely used for components in food machinery, pumps for liquid food, etc.Electrical: very good dielectric properties, halogen-free self-extinguishing power, weatherproof: these features make PVDF increasingly indispensable in this field.Mechanical: thanks to the low friction coefficient, it is ideal for bearings, even when operating in water.Information provided by Omnia Plastica s.p.a. for semifinished products such as sheet, rod, and tube.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO.1183 DIN.53479
Moisture Absorption at Equilibrium 0.00 %
0.00 %
50% relative humidity
Water Absorption at Saturation 0.00 %
0.00 %
23°C
Mechanical Properties Metric English Comments
Hardness, Rockwell R 62
62
dry sample; ISO2039.2
Ball Indentation Hardness 100 MPa
14500 psi
ISO2039.1 DIN.53456
Tensile Strength at Break 55.0 MPa
7980 psi
ISO.527 DIN.53455
Elongation at Break 300 %
300 %
ISO.527 DIN.53455
Tensile Modulus 2.00 GPa
290 ksi
ISO.527 DIN.53455
Compressive Strength 3.00 MPa
435 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Charpy Impact Unnotched NB
NB
7.5 J; ISO.R179 DIN.53453
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO179/3C DIN.53453
Coefficient of Friction, Dynamic 0.30
0.30
on dry ground steel; load =0.05MPa; speed =0.6 m/s
Thermal Properties Metric English Comments
CTE, linear 130 µm/m-°C

@Temperature 23.0 - 60.0 °C
72.2 µin/in-°F

@Temperature 73.4 - 140 °F
Thermal Conductivity 0.110 W/m-K
0.763 BTU-in/hr-ft²-°F
DIN.52612
Melting Point 180 °C
356 °F
Maximum Service Temperature, Air 140 °C
284 °F
Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C.
155 °C
311 °F
short period, no load
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO.75 DIN.53461
Minimum Service Temperature, Air -50.0 °C
-58.0 °F
impact conditions and heavy loads not considered
Flammability, UL94 V-0
V-0
Oxygen Index 43 %
43 %
ISO.4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ISO.93 DIN.53482
Dielectric Constant 8.0

@Frequency 1e+6 Hz
8.0

@Frequency 1e+6 Hz
ISO.250 DIN.53483
Dielectric Strength 120 kV/mm
3050 kV/in
ISO.243 DIN.53481
Dissipation Factor 0.060

@Frequency 1e+6 Hz
0.060

@Frequency 1e+6 Hz
ISO.250 DIN.53483