Old Hickory FC-120 Tennessee Ball Clay

Category	Ceramic , Clay , Ball Clay
Manufacturer	Old Hickory Clay Co.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Old Hickory FC-120 Tennessee Ball Clay.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The FC-120 clay is a special selection for sanitaryware. It is very fast casting and is designed to use in combination with the C-33A or other finer particle size distribution clay. The FC-120 provides excellent casting rate in a sanitaryware formula while maintaining a long plasticity range for trimming and finishing operations. The unique mineralogy of FC-120 also provides good dry strength by comparison to the fast casting rate.Information provided by Old Hickory Clay Company

Physical Properties	Metric	English	Comments
Particle Size	0.50 µm	0.50 µm	40% of particles less than
	1.0 µm	1.0 µm	51% of particles less than
	1.48 µm	1.48 µm	Median particle diameter
	<= 5.0 µm	<= 5.0 µm	77% of particles less than
pH	5.4	5.4
Soluble Sulfates	530 ppm	530 ppm
Specific Surface Area	18.3 m²/g	18.3 m²/g

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00410 GPa	0.595 ksi	Dry Modulus of Rupture, 50% clay/50% flint, cast bars

Thermal Properties	Metric	English	Comments
Shrinkage	4.5 %	4.5 %	Cone 04, Linear Fired Shrinkage
	6.0 %	6.0 %	Cone 3, Linear Fired Shrinkage
	8.0 %	8.0 %	Cone 11, Linear Fired Shrinkage
	8.5 %	8.5 %	Linear Drying Shrinkage

Component Elements Properties	Metric	English
Al2O3	26.34 %	26.34 %
CaO	0.13 %	0.13 %
Fe2O3	1.21 %	1.21 %
K2O	1.0 %	1.0 %
Loss on Ignition(%)	9.86 %	9.86 %
MgO	0.40 %	0.40 %
Na2O	0.080 %	0.080 %
SiO2	59.18 %	59.18 %
TiO2	1.8 %	1.8 %

Descriptive Properties	Value	Comments
Absorption (%)	15.8	Cone 04, Fired
	2.9	Cone 11, Fired
	9.9	Cone 3, Fired
CEC/MBI (meg/100 ml)	7
Crude Color	Light Brown
Filtration (ml)	31
Pyrometric Cone Equivalent (PCE)	29
Water of Plasticity (%)	35
Wet Sieve Residue (%)	0.57	Wet Sieve Residue, +200 mesh