Material Notes:
Data for polypropylene reinforced with 15% Nyco NYLITE® Wollastonite. Polypropylene used is Braskem TI6200Q High Impact Copolymer 20 MFR -NBWollastonite (calcium metasilicate, or CaSiO3) is a naturally occurring white, non-metallic mineral with an acicular or needle-shaped crystal structure. This distinctive property makes wollastonite an ideal performance mineral for a broad range of industrial and consumer applications.Information provided by NYCO Minerals.
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
ISO 1183
Filler Content 15 %
15 %
ISO 34351
Moisture Absorption 0.00300 %
0.00300 %
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Average
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 230 °C
13 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 21.0 MPa
3050 psi
50 mm/min - CH; ISO 527
Elongation at Break 120 %
120 %
50 mm/min - CH; ISO 527
Flexural Strength 28.0 MPa
4060 psi
2 mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
Charpy Impact, Notched 0.420 J/cm²

@Temperature -30.0 °C
2.00 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.40 J/cm²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 190 µm/m-°C

@Temperature -30.0 - 120 °C
106 µin/in-°F

@Temperature -22.0 - 248 °F
ISO 11359
CTE, linear, Transverse to Flow 187 µm/m-°C

@Temperature -30.0 - 120 °C
104 µin/in-°F

@Temperature -22.0 - 248 °F
ISO 11359
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
ISO 75