Nyco NYGLOS® 4W STO105 Wollastonite in Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Nyco
Trade Name NYGLOS®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nyco NYGLOS® 4W STO105 Wollastonite in Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data for polypropylene reinforced with 15% Nyco NYGLOS® 4W STO105 Wollastonite. Polypropylene used is Braskem TI6200Q High Impact Copolymer 20 MFR -NBWollastonite (calcium metasilicate, or CaSiO3) is a naturally occurring white, non-metallic mineral with an acicular or needle-shaped crystal structure. This distinctive property makes wollastonite an ideal performance mineral for a broad range of industrial and consumer applications.Information provided by NYCO Minerals.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Filler Content 15 %
15 %
ISO 34351
Moisture Absorption 0.00200 %
0.00200 %
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
Average
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 230 °C
14 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 20.0 MPa
2900 psi
50 mm/min - CH; ISO 527
Elongation at Break 130 %
130 %
50 mm/min - CH; ISO 527
Flexural Strength 27.0 MPa
3920 psi
2 mm/min; ISO 178
Flexural Modulus 2.015 GPa
292.3 ksi
2 mm/min; ISO 178
Charpy Impact, Notched 0.450 J/cm²

@Temperature -30.0 °C
2.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.60 J/cm²

@Temperature 23.0 °C
21.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -30.0 - 120 °C
36.7 µin/in-°F

@Temperature -22.0 - 248 °F
ISO 11359
CTE, linear, Transverse to Flow 64.0 µm/m-°C

@Temperature -30.0 - 120 °C
35.6 µin/in-°F

@Temperature -22.0 - 248 °F
ISO 11359
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ISO 75