NuSil MED-4165 Silicone, One Part High Consistent Elastomer - Restricted Medical Use

Category Polymer , Thermoset , Silicone
Manufacturer NuSil
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NuSil MED-4165 Silicone, One Part High Consistent Elastomer - Restricted Medical Use.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.Important Properties: HCRs with a peroxide cure system have a long history in implant applications. The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Features of peroxide cure high consistency rubbers include the following: One or two part Indefinite work timeHeat requiredAcid or alcohol byproductsPost cure required% shrinkage ~2 -5%Comments: UncatalyzedCure System: PeroxideInformation provided by NuSil
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
Typical
60 - 70
60 - 70
Certified
Tensile Strength at Break 6.20 MPa
899 psi
Certified
8.30 MPa
1200 psi
Typical
Tensile Stress 3.10 MPa

@Strain 200 %
450 psi

@Strain 200 %
Elongation at Break 450 %
450 %
Certified
500 %
500 %
Typical
Tear Strength 26.3 kN/m
150 pli
Certified
35.1 kN/m
200 pli
Typical
Processing Properties Metric English Comments
Cure Time 5.00 min

@Temperature 116 °C
0.0833 hour

@Temperature 241 °F
120 min

@Temperature 177 °C
2.00 hour

@Temperature 351 °F
Post
Descriptive Properties Value Comments
Mix Ratio 1 Part
Plasticity 115 mils