Nilit Polynil® C50L Externally Lubricated PA66/6

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer	Nilit
Trade Name	Polynil®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Polynil® C50L Externally Lubricated PA66/6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Polynil C50L shows better surface finish, flow and elongation than a comparable homopolymer. Key characteristics: Excellent flowHigh elongationGood impact strengthGood overall mechanical performanceGood thermal performance Information provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ASTM D792
Water Absorption	1.9 %	1.9 %	24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	9.0 %	9.0 %	sim. ISO 62
Loss On Ignition	28 %	28 %	ASTM D2863
Viscosity Measurement	50	50	relative viscosity (formic acid); ASTM D789
Linear Mold Shrinkage, Flow	0.013 cm/cm	0.013 in/in	Nilit

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D638
Elongation at Break	30 %	30 %	ASTM D638
Tensile Modulus	2.95 GPa	428 ksi	ASTM D638
Flexural Strength	115 MPa	16700 psi	ASTM D790
Flexural Modulus	2.80 GPa	406 ksi	ASTM D790
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	0.650 J/cm²	3.09 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F	ASTM D648
Vicat Softening Point	235 °C	455 °F	49 N; ASTM D1525
	245 °C	473 °F	9.8 N; ASTM D1525
Flammability, UL94	V-2 @Thickness 0.800 mm	V-2 @Thickness 0.0315 in
	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	18.0 kV/mm @Thickness 2.00 mm	457 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	>= 600 V	>= 600 V	UL 746

Descriptive Properties	Value	Comments
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309