Nilit Nilamid B3 H G7 35% Glass Fiber Reinforced PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer Nilit
Trade Name Nilamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid B3 H G7 35% Glass Fiber Reinforced PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid B3 H G7 is a general purpose, 35% glass fiber reinforced NYLON 6. It has high mechanical performance, and also excellent moldability. Its impact performance is outstanding, so it is often used in parts subjected to shock loads, like drill housings.Key characteristics: Good overall mechanical performanceEase of processingGood surface finishGood thermal performance up to 120°CGood overall chemical resistance against most solvents and detergentsInformation provided by NILIT.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792, ISO 1183
Water Absorption 0.90 %
0.90 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 190 MPa
27600 psi
ISO 527, ASTM D638
Elongation at Break 3.0 %
3.0 %
ISO 527, ASTM D638
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527, ASTM D638
Flexural Yield Strength 250 MPa
36300 psi
ISO 178, ASTM D790
150 MPa

@Temperature 90.0 °C
21800 psi

@Temperature 194 °F
ISO 178, ASTM D790
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178, ASTM D790
6.00 GPa

@Temperature 90.0 °C
870 ksi

@Temperature 194 °F
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
ISO 75, ASTM D648
Vicat Softening Point 218 °C
424 °F
49 N; ISO 306, ASTM D1525
222 °C
432 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Oxygen Index 23 %
23 %
ASTM D2863
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
650 °C

@Thickness 0.800 mm
1200 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Dielectric Strength 21.0 kV/mm

@Thickness 2.00 mm
533 kV/in

@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index 350 V

@Thickness 3.20 mm
350 V

@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
500 V

@Thickness 3.20 mm
500 V

@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 245 - 290 °C
473 - 554 °F
Zone 1 240 - 270 °C
464 - 518 °F
hopper
Zone 2 240 - 270 °C
464 - 518 °F
Zone 3 245 - 285 °C
473 - 545 °F
Zone 4 245 - 290 °C
473 - 554 °F
Melt Temperature 245 - 280 °C
473 - 536 °F
Do not melt above 310°C
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Flammability Rating B50
FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 MPa