Nilit Nilamid B3 H G6 30% Glass Fiber Reinforced PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Nilit
Trade Name	Nilamid
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Nilamid B3 H G6 30% Glass Fiber Reinforced PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Nilamid B3 H G6 is a general purpose, 30% glass fiber reinforced NYLON 6 with a combination of good mechanical performance, impact strength and processability. It is one of the most widely used engineering plastics.Key characteristics: Good overall mechanical performanceEase of processingGood surface finishGood thermal performance up to 120°CGood overall chemical resistance against most solvents and detergentsInformation provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	ASTM D792, ISO 1183
Water Absorption	1.0 %	1.0 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	6.5 %	6.5 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	Euronil
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	Euronil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	180 MPa	26100 psi	ISO 527, ASTM D638
Elongation at Break	3.0 %	3.0 %	ISO 527, ASTM D638
Tensile Modulus	9.50 GPa	1380 ksi	ISO 527, ASTM D638
Flexural Yield Strength	230 MPa	33400 psi	ISO 178, ASTM D790
	140 MPa @Temperature 90.0 °C	20300 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	8.70 GPa	1260 ksi	ISO 178, ASTM D790
	5.00 GPa @Temperature 90.0 °C	725 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	9.50 kJ/m² @Temperature -30.0 °C	4.52 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	ISO 179
	4.00 J/cm² @Temperature -30.0 °C	19.0 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²	ISO 179
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	105 °C	221 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	221 °C	430 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ISO 75, ASTM D648
Vicat Softening Point	218 °C	424 °F	49 N; ISO 306, ASTM D1525
	222 °C	432 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Oxygen Index	23 %	23 %	ASTM D2863
Glow Wire Test	650 °C @Thickness 3.20 mm	1200 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	650 °C @Thickness 0.800 mm	1200 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12

Electrical Properties	Metric	English	Comments
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	350 V @Thickness 3.20 mm	350 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	500 V @Thickness 3.20 mm	500 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A

Processing Properties	Metric	English	Comments
Nozzle Temperature	245 - 290 °C	473 - 554 °F
Zone 1	240 - 270 °C	464 - 518 °F	hopper
Zone 2	240 - 270 °C	464 - 518 °F
Zone 3	245 - 285 °C	473 - 545 °F
Zone 4	245 - 290 °C	473 - 554 °F
Melt Temperature	245 - 280 °C	473 - 536 °F	Do not melt above 310°C
Mold Temperature	90.0 - 110 °C	194 - 230 °F	Preferred
Drying Temperature	80.0 - 85.0 °C	176 - 185 °F
Dry Time	4 hour	4 hour
Injection Pressure	70.0 - 100 MPa	10200 - 14500 psi

Descriptive Properties	Value	Comments
Clamping Force	in tons, 0.7 times the projected surface area in cm²
Flammability Rating	B50	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 MPa