Nilit Nilamid B3 H G3 15% Glass Fiber Reinforced PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer	Nilit
Trade Name	Nilamid
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Nilamid B3 H G3 15% Glass Fiber Reinforced PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Nilamid B3 H G3 is a general purpose, 15% glass fiber reinforced NYLON 6. These products combine good overall mechanical performance and impact strength with ease of processing. Key characteristics: Good overall mechanical performanceEase of processing Good surface finishGood thermal performance up to 120°CGood overall chemical resistance against most solvents and detergents Information provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in³	ASTM D792, ISO 1183
Water Absorption	2.0 %	2.0 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	7.0 %	7.0 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	Euronil
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	Euronil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	130 MPa	18900 psi	ISO 527, ASTM D638
Elongation at Break	4.0 %	4.0 %	ISO 527, ASTM D638
Tensile Modulus	5.80 GPa	841 ksi	ISO 527, ASTM D638
Flexural Yield Strength	180 MPa	26100 psi	ISO 178, ASTM D790
	110 MPa @Temperature 90.0 °C	16000 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	5.50 GPa	798 ksi	ISO 178, ASTM D790
	2.05 GPa @Temperature 90.0 °C	297 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	3.00 kJ/m² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	4.00 kJ/m² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	3.50 J/cm²	16.7 ft-lb/in²	ISO 179
	2.50 J/cm² @Temperature -30.0 °C	11.9 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179
	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	100 °C	212 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	215 °C	419 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ISO 75, ASTM D648
Vicat Softening Point	210 °C	410 °F	49 N; ISO 306, ASTM D1525
	220 °C	428 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Oxygen Index	22 %	22 %	ASTM D2863
Glow Wire Test	650 °C @Thickness 0.800 mm	1200 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12
	750 °C @Thickness 3.20 mm	1380 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12

Electrical Properties	Metric	English	Comments
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	375 V @Thickness 3.20 mm	375 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	500 V @Thickness 3.20 mm	500 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A

Processing Properties	Metric	English	Comments
Nozzle Temperature	245 - 290 °C	473 - 554 °F
Zone 1	240 - 270 °C	464 - 518 °F	hopper
Zone 2	240 - 270 °C	464 - 518 °F
Zone 3	245 - 285 °C	473 - 545 °F
Zone 4	245 - 290 °C	473 - 554 °F
Melt Temperature	245 - 280 °C	473 - 536 °F	Do not melt above 310°C
Mold Temperature	90.0 - 110 °C	194 - 230 °F	Preferred
Drying Temperature	80.0 - 85.0 °C	176 - 185 °F
Dry Time	4 hour	4 hour
Injection Pressure	70.0 - 100 MPa	10200 - 14500 psi

Descriptive Properties	Value	Comments
Clamping Force	in tons, 0.7 times the projected surface area in cm²
Flammability Rating	B22	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 MPa