Nilit Nilamid B G6 FR HF 30% Glass Fiber Reinforced, Flame Retardant PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Nilit
Trade Name	Nilamid
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Nilamid B G6 FR HF 30% Glass Fiber Reinforced, Flame Retardant PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Nilamid B G6 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price/performance ratio and can be colored in almost any color. It does not cause any corrosion of or deposits on electrical contacts. Laser marking grades with a very good contrast are available.Key characteristics: UL 94 V2 at 0.75 mmHalogen and red phosphorous freeGood overall mechanical performanceLow densityColorable in a wide range of colorsEasy processing, fast cyclingNo corrosion of or deposits on electrical contactsInformation provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/in³	ASTM D792, ISO 1183
Water Absorption	1.0 %	1.0 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	5.5 %	5.5 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	Euronil
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	Euronil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527, ASTM D638
Elongation at Break	3.0 %	3.0 %	ISO 527, ASTM D638
Flexural Yield Strength	145 MPa	21000 psi	ISO 178, ASTM D790
	95.0 MPa @Temperature 90.0 °C	13800 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	7.60 GPa	1100 ksi	ISO 178, ASTM D790
	3.25 GPa @Temperature 90.0 °C	471 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	3.00 kJ/m² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	5.00 kJ/m² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	2.50 J/cm²	11.9 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	110 °C	230 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	215 °C	419 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	191 °C	376 °F	ISO 75, ASTM D648
Vicat Softening Point	210 °C	410 °F	49 N; ISO 306, ASTM D1525
	217 °C	423 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	V-2 @Thickness 0.800 mm	V-2 @Thickness 0.0315 in
	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in
Oxygen Index	24 %	24 %	ASTM D2863
Glow Wire Test	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12

Electrical Properties	Metric	English	Comments
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	550 V @Thickness 3.20 mm	550 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A
	550 V @Thickness 3.20 mm	550 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A

Descriptive Properties	Value	Comments
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Needle Test	OK	IEC 695-2-2, 1 or 2 mm