Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Nilit
Trade Name Nilamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid B G4 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price/performance ratio and can be colored in almost any color. It does not cause any corrosion of or deposits on electrical contacts. Laser marking grades with a very good contrast are available.Key characteristics: UL 94 V2 at 0.75 mmHalogen and red phosphorous freeGood overall mechanical performanceLow densityColorable in a wide range of colorsEasy processing, fast cyclingNo corrosion of or deposits on electrical contacts Information provided by NILIT.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792, ISO 1183
Water Absorption 1.2 %
1.2 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 6.5 %
6.5 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527, ASTM D638
Elongation at Break 3.0 %
3.0 %
ISO 527, ASTM D638
Tensile Modulus 5.50 GPa
798 ksi
ISO 527, ASTM D638
Flexural Yield Strength 130 MPa
18900 psi
ISO 178, ASTM D790
85.0 MPa

@Temperature 90.0 °C
 12300 psi

@Temperature 194 °F
 ISO 178, ASTM D790
Flexural Modulus 6.00 GPa
870 ksi
ISO 178, ASTM D790
2.60 GPa

@Temperature 90.0 °C
 377 ksi

@Temperature 194 °F
 ISO 178, ASTM D790
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
ISO 75, ASTM D648
Vicat Softening Point 206 °C
403 °F
49 N; ISO 306, ASTM D1525
215 °C
419 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
Oxygen Index 25 %
25 %
ASTM D2863
Glow Wire Test 960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 Glow Wire Flammability Index; IEC 694-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Dielectric Strength 21.0 kV/mm

@Thickness 2.00 mm
 533 kV/in

@Thickness 0.0787 in
 ASTM D149
Comparative Tracking Index 550 V

@Thickness 3.20 mm
 550 V

@Thickness 0.126 in
 Sol. A; IEC 112, UL 746A
550 V

@Thickness 3.20 mm
 550 V

@Thickness 0.126 in
 Sol. B; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 245 - 265 °C
473 - 509 °F
Zone 1 235 - 255 °C
455 - 491 °F
hopper
Zone 2 240 - 265 °C
464 - 509 °F
Zone 3 245 - 265 °C
473 - 509 °F
Zone 4 245 - 265 °C
473 - 509 °F
Melt Temperature 240 - 260 °C
464 - 500 °F
Do not melt above 275°C
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80°C is Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Flammability Rating SE
FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 MPa
Needle Test OK
IEC 695-2-2, 1 or 2 mm