- Nilit Nilamid B FR HF Unfilled, Flame Retardant, Halogen and Red Phosphorous Free PA6
Nilit Nilamid B FR HF Unfilled, Flame Retardant, Halogen and Red Phosphorous Free PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid B FR HF Unfilled, Flame Retardant, Halogen and Red Phosphorous Free PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid B FR HF is an unfilled, flame retardant NYLON 6 with excellent flow characteristics, outstanding elongation and impact strength and a good thermal performance. Because of its excellent processing characteristics it is often used in complicated components. Typical applications include electrical cooling fans and housings, fuse boxes and carriers, flame retardant cable ties and corrugated tube. This product can be supplied in a full range of colors and has an excellent surface finish. For this reason it is often used in aesthetical components, like public bathroom accessories or trash cans.Key characteristics: Easy processingGood heat aging characteristics: UL RTI listing (mechanical) up to 140°CV0 listing at 0.75 mmHalogen and red phosphorous freeExcellent CTI value (600 V)Good impact strengthGood elongation Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 2.0 % | 2.0 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 9.0 % | 9.0 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527, ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527, ASTM D638 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 115 MPa | 16700 psi | ISO 178, ASTM D790 |
| 50.0 MPa @Temperature 90.0 °C |
7250 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178, ASTM D790 |
| 0.700 GPa @Temperature 90.0 °C |
102 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 12.0 J/cm² | 57.1 ft-lb/in² | ISO 179 |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 196 °C | 385 °F | 49 N; ISO 306, ASTM D1525 |
| 210 °C | 410 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 29 % | 29 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 550 V @Thickness 3.20 mm |
550 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| 600 V @Thickness 3.20 mm |
600 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 235 - 265 °C | 455 - 509 °F | |
| Zone 1 | 225 - 250 °C | 437 - 482 °F | hopper |
| Zone 2 | 230 - 265 °C | 446 - 509 °F | |
| Zone 3 | 235 - 265 °C | 455 - 509 °F | |
| Zone 4 | 235 - 265 °C | 455 - 509 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Do not melt above 275°C |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | 80°C is Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa | |
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm |