Nilit Nilamid A3 N H2 Nucleated, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid A3 N H2 Nucleated, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid A3 N H2 is a nucleated, heat stabilized NYLON 66 with excellent flow characteristics and very fast cycle time. It is widely used throughout many industries for mass production articles that require fast cycle times and good resistance against thermal aging, like for instance terminal blocks or automotive connectors.Key characteristics: Excellent flowFast cycle timeHigh elongationGood mould release High toughnessGood thermal performanceUL 94 V2 listed down to 0.75 mm Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527, ASTM D638 |
| Elongation at Break | >= 40 % | >= 40 % | ISO 527, ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527, ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 115 MPa | 16700 psi | ISO 178, ASTM D790 |
| 35.0 MPa @Temperature 90.0 °C |
5080 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178, ASTM D790 |
| 0.750 GPa @Temperature 90.0 °C |
109 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 4.50 kJ/m² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 115 °C | 239 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 245 °C | 473 °F | 49 N; ISO 306, ASTM D1525 |
| 255 °C | 491 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
||
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
||
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Glow Wire Test | 850 °C @Thickness 0.800 mm |
1560 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 850 °C @Thickness 3.20 mm |
1560 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 550 V @Thickness 3.20 mm |
550 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| 600 V @Thickness 3.20 mm |
600 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 265 - 295 °C | 509 - 563 °F | |
| Zone 1 | 260 - 290 °C | 500 - 554 °F | hopper |
| Zone 2 | 265 - 290 °C | 509 - 554 °F | |
| Zone 3 | 265 - 290 °C | 509 - 554 °F | |
| Zone 4 | 265 - 295 °C | 509 - 563 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Do not melt above 300°C |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | 80°C is Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 Mpa |