Nilit Nilamid A3 H ZC High Impact PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Nilit
Trade Name Nilamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid A3 H ZC High Impact PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid A3 H ZC has outstanding impact performance, even at minus temperatures. It is widely used for components subjected to high shock loads. Applications include bicycle components, garden equipment, components in the car interior and industrial machine components.Key characteristics: outstanding impact strength, even at minus temperaturesHigh elongation Easy processingGood surface finishInformation provided by NILIT.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792, ISO 1183
Water Absorption 1.0 %
1.0 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 7.0 %
7.0 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 52.0 MPa
7540 psi
ISO 527, ASTM D638
Elongation at Break >= 70 %
>= 70 %
ISO 527, ASTM D638
Elongation at Yield 9.0 %
9.0 %
ISO 527, ASTM D638
Flexural Yield Strength 70.0 MPa
10200 psi
ISO 178, ASTM D790
Flexural Modulus 1.90 GPa
276 ksi
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
65.0 kJ/m²

@Temperature 23.0 °C
30.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179
1.80 J/cm²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 65.0 °C
149 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75, ASTM D648
Vicat Softening Point 200 °C
392 °F
49 N; ISO 306, ASTM D1525
250 °C
482 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Oxygen Index 20 %
20 %
ASTM D2863
Glow Wire Test 550 °C

@Thickness 0.800 mm
1020 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Dielectric Strength 21.0 kV/mm

@Thickness 2.00 mm
533 kV/in

@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index 600 V

@Thickness 3.20 mm
600 V

@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
600 V

@Thickness 3.20 mm
600 V

@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 275 - 290 °C
527 - 554 °F
Zone 1 265 - 285 °C
509 - 545 °F
hopper
Zone 2 270 - 285 °C
518 - 545 °F
Zone 3 275 - 290 °C
527 - 554 °F
Zone 4 275 - 290 °C
527 - 554 °F
Melt Temperature 275 - 290 °C
527 - 554 °F
Do not melt above 300°C
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80°C is Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 Mpa