Nilit FRIANYL B63 W-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 W-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 158 MPa | 22900 psi | ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 5.80 GPa | 841 ksi | ISO 527 |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.10 J/cm² | 14.8 ft-lb/in² | DIN 53453 |
| 3.00 J/cm² @Temperature -40.0 °C |
14.3 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- LATI LATAMID 12 H FE85 Nylon 12 Base Magnetizable Compound (discontinued **)
- Lubriplate SYNX HD-2 Calcium Sulfonate Complex Multi-Purpose Grease
- KKPC KOSYN KNB 25M Acrylonitrile Butadiene Rubber (NBR)
- A. Schulman POLYBATCH™ Dark Blue Oil LL40350/4 Concentrate Based In LLDPE
- Hexcel® HexPly® ES70 120°C Curing Epoxy Matrix, Hybrid carbon/Aramid fabric 245 g/m2
- Eagle Brass 706 Copper Nickel 10%, 1/2 Hard
- Dow Corning SILASTIC® LS 5-2040 FLUOROSILICONE RUBBER
- AlphaGary Evoprene™ G 3315 SEBS Thermoplastic Elastomer
- Asahi Kasei Thermylene® P6-30FM-Y249B 30% Glass/Mineral Reinforced, Heat Stabilized
- ACC EP MAP-7.5 EPI Engineered Polymers Aliphatic Polymer
Copyright © lookpolymers.com All Rights Reserved