- Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled
Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 132 MPa | 19100 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527 |
| Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| 0.350 J/cm² @Temperature -40.0 °C |
1.67 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne FireCon™ CPE 0883-01 RoHS BLACK Polyethylene, Chlorinated (CPE)
- Polimeri Europa Extir® P 1212 Expandable Polystyrene, Special Purpose (discontinued **)
- Shandong Rike Chemical ACM-1 PVC Impact Modifier ACM Resin
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Black Peroxide Cure
- ExxonMobil Hicor® 30 HF 104 OHD Film
- Daikin POLYFLON FA-500 MPA, White Powder
- BASF Formic Acid - 99-100%
- BASF Ultradur B 4300 G2 High Speed Unc. 10% Glass Filled PBT
- Plastcom SLOVALEN PC 92 T 40 PP, 40% mineral filling
Copyright © lookpolymers.com All Rights Reserved