Nilit FRIANYL B63 KF50 Nylon 6 for injection molding, 50% short glass fiber reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Nilit (formerly Frisetta Polymer)
Trade Name FRIANYL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit FRIANYL B63 KF50 Nylon 6 for injection molding, 50% short glass fiber reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 1.5 - 2.5 %
1.5 - 2.5 %
ISO 62
Water Absorption at Saturation 7.0 - 8.0 %
7.0 - 8.0 %
ISO 62
Viscosity Measurement 145
145
Viscosity index; ISO 307
Linear Mold Shrinkage 0.0040 - 0.011 cm/cm
0.0040 - 0.011 in/in
FRISETTA Test Method
Mechanical Properties Metric English Comments
Ball Indentation Hardness 190 MPa
27600 psi
ISO 2039-1
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ISO 527
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
DIN 53453
1.40 J/cm²

@Temperature -40.0 °C
6.66 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
DIN 53453
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
ISO 3146 DSC
Maximum Service Temperature, Air 120 °C
248 °F
Continuous; FRISETTA Test Method
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
IEC 250
Comparative Tracking Index 575 V
575 V
CTI 100; IEC 112