Nilit FRIANYL B63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, good conductive and electrostatic properties.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0060 - 0.016 cm/cm | 0.0060 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 7.90 GPa | 1150 ksi | ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | DIN 53453 |
| 2.70 J/cm² @Temperature -40.0 °C |
12.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
Users viewing this material also viewed the following:
- RheTech Products T40P250-00 40% Talc Reinforced Polypropylene Copolymer, Natural
- Polykemi AB SCANMID 6 B12^ NH6 Nylon 6, Flame Retardant, Halogen Free
- Lehmann & Voss LUVOCOM® 1106-8032/GY Polyether imide, unreinforced, laser markable
- Struktol VP 3643 Optimized elastomer-modified epoxy prepolymer
- Silberline Sparkle Silvet® 790-30-E1
- 3M AC-665 Class C-12 Aerospace Sealant
- Beijing Chemical Industry KAIFA® HN301-G10 PA6 Resin
- Amity Thermosets ATS 1613-G Phenolic Molding Nylon and inorganic Filler, Compression Molded
- 3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride
- A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound
Copyright © lookpolymers.com All Rights Reserved