- Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.015 cm/cm | 0.0070 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | DIN 53453 |
| 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU | |
| 1.70 J/cm² @Temperature -40.0 °C |
8.09 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 | |
| 0.500 J/cm² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering C70H Chloroprene Rubber
- SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific)
- SABIC Innovative Plastics Lexan® EM3110R PC
- SABIC Innovative Plastics Lexan® FXG171R PC (Europe-Africa-Middle East)
- Solvay Specialty Polymers Ryton® R-7-121BL Polyphenylene Sulfide (PPS), GlassMineral Filled
- Zoltek Panex 30® Low Oxidation Knitted Carbon Fabric
- Eastman Drystar 0113 Copolyester
- Dow Corning XIAMETER® PMCPPMX-200 1CS Silicone Fluid
- Asahi Glass Fluon® P-62XP PFA Perfluoropolymer
- Aremco Ceramabond™ 569 High Temperature Ceramic Adhesive/Paste, Alumina Filled
Copyright © lookpolymers.com All Rights Reserved