Nilit FRIANYL A63 H-KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Nilit (formerly Frisetta Polymer)
Trade Name FRIANYL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit FRIANYL A63 H-KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 1.5 - 2.5 %
1.5 - 2.5 %
ISO 62
Water Absorption at Saturation 6.0 - 8.0 %
6.0 - 8.0 %
ISO 62
Viscosity Measurement 145
145
Viscosity index; ISO 307
Linear Mold Shrinkage 0.0050 - 0.015 cm/cm
0.0050 - 0.015 in/in
FRISETTA Test Method
Mechanical Properties Metric English Comments
Ball Indentation Hardness 175 MPa
25400 psi
ISO 2039-1
Tensile Strength at Break 85.0 MPa
12300 psi
ISO 527
Elongation at Break 4.0 %
4.0 %
ISO 527
Tensile Modulus 4.50 GPa
653 ksi
ISO 527
Flexural Strength 115 MPa
16700 psi
ISO 178
Flexural Modulus 3.80 GPa
551 ksi
ISO 178
Charpy Impact Unnotched 1.90 J/cm²
9.04 ft-lb/in²
DIN 53453
3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eU
1.40 J/cm²

@Temperature -40.0 °C
6.66 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
DIN 53453
0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 3146 DSC
Maximum Service Temperature, Air 130 °C
266 °F
Continuous; FRISETTA Test Method
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
IEC 250
Comparative Tracking Index 550 V
550 V
CTI 100; IEC 112