Network Polymers Softflex® 7000
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 7000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0040 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0030 - 0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 18.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
18.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 100.2 g/10 min @Load 1.00 kg, Temperature 235 °C |
100.2 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 67 - 77 | 67 - 77 | Instantaneous; ASTM D2240 |
| Tensile Strength, Yield | 24.7 MPa | 3580 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 730 % | 730 % | ASTM D412 |
| 50% Modulus | 0.00210 GPa | 0.305 ksi | ASTM D412 |
| 100% Modulus | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 300% Modulus | 0.00520 GPa | 0.754 ksi | ASTM D412 |
| Tear Strength | 66.5 kN/m | 379 pli | |
| Taber Abrasion, mg/1000 Cycles | 3.0 | 3.0 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 25 % | 25 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® Shock Seal™ 4790-79-9 Handheld Urethane Foam, Handheld Grade, PET Reinforced
- LyondellBasell Alathon® L5332CP High Density Polyethylene, Blow Molding Grade
- Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (480°C (900°F) - 1 hour - air cooling)
- Solvay Specialty Polymers FOMBLIN® Z25 PFPE Lubricant
- Wellman Wellamid® GF1811-BK1 15% Glass Fiber Reinforced Nylon 66
- Hexcel® HexTow™ AS7 Carbon Fiber
- Dow 722 Low Density Polyethylene (LDPE)
- Axiall 384FR Wire & Cable Flexible PVC
- Dow Corning XIAMETER® PMCPMEM-0062 Emulsion PS
Copyright © lookpolymers.com All Rights Reserved