Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Nabaltec APYRAL® 60D Al(OH)3

Category Ceramic , Oxide , Aluminum Oxide , Other Engineering Material , Additive/Filler for Polymer
Manufacturer Nabaltec GmbH
Trade Name APYRAL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nabaltec APYRAL® 60D Al(OH)3.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
APYRAL ® from Nabaltec is an environmentally friendly halogen free product which is used as a flame retardant filler in a wide variety of rubber and polymeric materials. During thermal decomposition APYRAL ® does not generate toxic or corrosive gases. In addition, there is a distinct reduction in smoke density. APYRAL ® is effective in the crucial phase of the burning process before the outbreak of a fully developed fire.APYRAL ® can be used as a flame retardant filler in ThermosetsElastomersThermoplasticsCable CompoundsTechnical Rubber CompoundsPressed and cast Plastic PartsThermal Insulation FoamsGlass-fiber reinforced plastics
Physical Properties Metric English Comments
Bulk Density 0.350 g/cc
0.0126 lb/in³
Density 2.40 g/cc
0.0867 lb/in³
Brightness 98 %

@Wavelength 457 nm
98 %

@Wavelength 457 nm
Whiteness; Elrepho
Oil Absorption 33 %
33 %
ml/100 g
Moisture Absorption at Equilibrium 0.30 %
0.30 %
Loss On Ignition 34.6 %

@Temperature 105 - 1000 °C
34.6 %

@Temperature 221 - 1830 °F
Particle Size 1.0 µm
1.0 µm
Median Grain Diameter
Specific Surface Area 6.0 m²/g
6.0 m²/g
BET
Mechanical Properties Metric English Comments
Hardness, Mohs 3
3
Optical Properties Metric English Comments
Refractive Index 1.58
1.58
Component Elements Properties Metric English Comments
Fe2O3 0.010 %
0.010 %
Na2O 0.40 %
0.40 %
SiO2 0.010 %
0.010 %
Electrical Properties Metric English Comments
Electrical Resistivity 20000 ohm-cm
20000 ohm-cm
Descriptive Properties Value Comments
Al(OH)3 wt % 99.5
Crystal Structure Gibbsite
Mechanical Properties as Additive Elongation at break: 160 %
MVR: 1.6 cm3/10min
Tensile Strength: 14.2 Mpa
HFFR-EVA cable compound
Sieve Analysis (%) 0.02
> 45 µm