NOVA Chemicals Surpass® RMs341-U Octene sHDPE Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Rotational Molding Grade
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® RMs341-U Octene sHDPE Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RMs341-U complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. RMs341-U is subject to the specific limitation that it may contact food only at temperatures of 212°F and below.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Octene copolymer, Exceptional low temperature impact properties, Broad processing window, Low viscosity for exceptional processability yielding shorter cycle times and energy savings, Superior whiteness for improved part appearance, Easy mold release, NSF listed for standards 24, 51 and 61, UL 94 HBAdditives: Processing antioxidants, UV stabilizersApplications: OEM custom and proprietary components, Recreational and leisure equipment, Containers, Septic tanks, Fish boxes, Large tanks
Physical Properties Metric English Comments
Density 0.941 g/cc
0.0340 lb/in³
ASTM D 792
ESCR 100% Igepal® >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
Bent Strip, Condition B, F50 Values from compression molded samples; ASTM D 1693
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 20.2 MPa
2930 psi
Type IV specimen, 2" per minute test speed, 0.075" thickness compression molded samples; ASTM D 638
Elongation at Yield 12 %
12 %
Type IV specimen, 2" per minute test speed, 0.075" thickness compression molded samples; ASTM D 638
Flexural Modulus, 1% Secant 827 MPa
120000 psi
From compression molded samples; ASTM D 790
Impact Test 95.0 J

@Thickness 3.17 mm,
Temperature -40.0 °C
70.1 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM Low Temperature Impact on Rotomolded samples; ARM Method
230 J

@Thickness 6.35 mm,
Temperature -40.0 °C
170 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM Low Temperature Impact on Rotomolded samples; ARM Method
Thermal Properties Metric English Comments
Melting Point 126 °C
259 °F
ASTM E 794
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 43.0 °C
109 °F
ASTM D 648