NOVA Chemicals Surpass® HPs900-C Octene sLLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	NOVA Chemicals
Trade Name	Surpass®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Surpass® HPs900-C Octene sLLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Easy processabilityExceptional clarity and glossLow gelExcellent seal properties Applications: High clarity applications Lamination film Coextruded sealant layerHigh toughness filmInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³	ASTM D792
Thickness	25.0 microns	0.984 mil
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.03 MPa	1310 psi	ASTM D882
Film Tensile Strength at Yield, TD	9.03 MPa	1310 psi	ASTM D882
Film Elongation at Yield, MD	520 %	520 %	ASTM D638
Film Elongation at Yield, TD	750 %	750 %	ASTM D882
Puncture Energy	2.10 J	1.55 ft-lb	Low Friction Puncture
Elmendorf Tear Strength MD	280 g	280 g	ASTM D1922
Elmendorf Tear Strength TD	445 g	445 g	ASTM D1922
Dart Drop Test	>= 800 g	>= 1.76 lb	ASTM D1709/A
Film Tensile Strength at Break, MD	49.0 MPa	7110 psi	ASTM D882
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882
1% Secant Modulus, MD	135.0 MPa	19580 psi	ASTM D882
1% Secant Modulus, TD	155.0 MPa	22480 psi	ASTM D882
Heat Seal Strength Initiation Temperature	100 °C	212 °F	2N

Optical Properties	Metric	English	Comments
Haze	4.0 %	4.0 %	ASTM D1003
Gloss	79 %	79 %	at 45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	185 - 200 °C	365 - 392 °F