NOVA Chemicals Surpass® FPs225-A Octene Copolymer sLLDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® FPs225-A Octene Copolymer sLLDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FPs225-A complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without temperature or food-type restrictions, subject to technical suitability.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Excellent tensile and elongation properties, Good optical properties, Low gel levelAdditives: High temperature AOApplications: Co-extrusion and laminationFilm properties are typical of cast film extruded at a melt temperature of 500°F, and a line speed of 800 ft/min.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D 792
Thickness 20.0 microns
0.787 mil
As tested for properties on this data sheet
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.2 MPa
1480 psi
ASTM D 882
Film Tensile Strength at Yield, TD 9.80 MPa
1420 psi
ASTM D 882
Film Elongation at Break, MD 440 %
440 %
ASTM D 882
Film Elongation at Break, TD 780 %
780 %
ASTM D 882
Elmendorf Tear Strength MD 190 g
190 g
ASTM D 1922
Elmendorf Tear Strength TD 440 g
440 g
ASTM D 1922
Elmendorf Tear Strength, MD 9.50 g/micron
241 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 22.0 g/micron
559 g/mil
ASTM D 1922
Dart Drop 4.50 g/micron
114 g/mil
ASTM D 1709/A
Dart Drop Test 90.0 g
0.198 lb
F50; ASTM D 1709/A
Film Tensile Strength at Break, MD 34.0 MPa
4930 psi
ASTM D 882
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D 882
1% Secant Modulus, MD 160 MPa
23200 psi
ASTM D 882
1% Secant Modulus, TD 170 MPa
24700 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 2.3 %
2.3 %
ASTM D 1003
Gloss 84 %
84 %
At 45°; ASTM D 2457
Descriptive Properties Value Comments
Low Friction Puncture 60 (J/mm)
NOVA Chemicals test method (highlight instrumented stretch wrapper)