NOVA Chemicals Surpass® FPs117-C Octene Copolymer sLLDPE Film Resins

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® FPs117-C Octene Copolymer sLLDPE Film Resins.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FPs117-C complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without temperature or food-type restrictions, subject to technical suitability.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Easy processability, Superior toughness with excellent tear strength, Excellent seal properties, Low gelAdditives: Antioxidant, Polymer process aidApplications: Lamination film, Co-extruded sealant layer, and high toughness filmFilm properties are typical of blown film extruded on a 2.5" extruder with 4" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions.
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D 792
Thickness 25.0 microns
0.984 mil
As tested for properties on this data sheet
12.7 - 76.0 microns
0.500 - 2.99 mil
Recommended range for processing
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ASTM D 882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D 882
Film Elongation at Break, MD 540 %
540 %
ASTM D 882
Film Elongation at Break, TD 760 %
760 %
ASTM D 882
Elmendorf Tear Strength MD 300 g
300 g
ASTM D 1922
Elmendorf Tear Strength TD 450 g
450 g
ASTM D 1922
Elmendorf Tear Strength, MD 12.0 g/micron
305 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 18.0 g/micron
457 g/mil
ASTM D 1922
Dart Drop 16.0 g/micron
406 g/mil
ASTM D 1709/A
Dart Drop Test 400 g
0.882 lb
F50; ASTM D 1709/A
Film Tensile Strength at Break, MD 46.0 MPa
6670 psi
ASTM D 882
Film Tensile Strength at Break, TD 42.0 MPa
6090 psi
ASTM D 882
1% Secant Modulus, MD 126 MPa
18300 psi
ASTM D 882
1% Secant Modulus, TD 132 MPa
19100 psi
ASTM D 882
Heat Seal Strength Initiation Temperature 100 °C
212 °F
Temperature at which a 2-mil film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed.
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
LDPE blended; ASTM D 1003
16 %
16 %
100% LLDPE; ASTM D 1003
Gloss 37 %
37 %
At 45°, 100% LLDPE; ASTM D 2457
72 %
72 %
At 45°, LDPE blended; ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 180 - 200 °C
356 - 392 °F
Recommended
Die Opening 0.0889 - 0.216 cm
0.0350 - 0.0850 in
Recommended range
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0
Optimum range
Descriptive Properties Value Comments
Low Friction Puncture 79 (J/mm)
NOVA Chemicals test method