NOVA Chemicals Sclair® 17A Butene HDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 17A Butene HDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
17A complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without temperature or food-type restrictions, subject to technical suitability.NOVA Chemicals' polyethylene resins are chemically and biologically inert.Features: Low gel, Good processabilityAdditives: Process stabilizerApplications: Co-extrusions, BlendingProperties measured from film produced on a laboratory extruder with a 4 inch die, 35 mil die gap, and a BUR of 2.5:1
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ASTM D 792
Oxygen Transmission Rate 1920 cc/m²/day
124 cc/100 in²/day
0% RH; ASTM D 1434
Thickness 38.0 microns
1.50 mil
Melt Flow 0.45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Shore D 67
67
ASTM D 2240
Film Tensile Strength at Yield, MD 22.0 MPa
3190 psi
ASTM D 882
Film Tensile Strength at Yield, TD 20.0 MPa
2900 psi
ASTM D 882
Film Elongation at Break, MD 650 %
650 %
ASTM D 882
Film Elongation at Break, TD 750 %
750 %
ASTM D 882
Coefficient of Friction 0.24
0.24
ASTM D 1894
Elmendorf Tear Strength MD 22 g
22 g
ASTM D 1922
Elmendorf Tear Strength TD 875 g
875 g
ASTM D 1922
Elmendorf Tear Strength, MD 0.600 g/micron
15.2 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 23.0 g/micron
584 g/mil
Dart Drop Test 40.0 g
0.0882 lb
1.1; ASTM D 1709/A
Film Tensile Strength at Break, MD 45.0 MPa
6530 psi
ASTM D 882
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ASTM D 882
1% Secant Modulus, MD 630 MPa
91400 psi
ASTM D 882
1% Secant Modulus, TD 900 MPa
131000 psi
ASTM D 882
Thermal Properties Metric English Comments
Vicat Softening Point 125 °C
257 °F
ASTM D 1525
Descriptive Properties Value Comments
Low Friction Puncture (J/mm) 23
NOVA Chemicals Test Method
Moisture Vapor Transmission Rate (g/m²/24h) 4
At 38°C, 100% RH