NOVA Chemicals Sclair® 14J1 Octene LMDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 14J1 Octene LMDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, good clarity, high strength and toughness.Applications: Produce film.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 820 % | 820 % | ASTM D882 |
| Secant Modulus, MD | 0.400 GPa | 58.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.500 GPa | 72.5 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.0 g/micron | 356 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Nye Lubricants 760A (NG) Synthetic Oil
- Lanxess Durethan® BM 25 FN20 700350 Nylon 6, 25% Mineral
- Silberline A-6240
- Sharadaa Ceramics REFCAST HA PLUS High Alumina Castables
- Borealis Borclean™ HB300BF Polypropylene Homopolymer for Capacitor Film
- Wellman Wellamid® MRGFX1393-N 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6
- Westlake Epolene® E-20 Emulsifiable - Oxidized Low Molecular Weight Polyethylene Polymer
- ExxonMobil Exxtral™ CNT 001W Performance Polyolefin
- Eurotec® Tecomid® NA40 NL IL PA6.6, impact modified, natural
- Wall Colmonoy COLMONOY® 4 PTA - Nickel-Base Hard Surfacing Alloy With Chromium Boride
Copyright © lookpolymers.com All Rights Reserved