NOVA Chemicals Sclair® 14A Butene MDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 14A Butene MDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, strength and toughness, broad MW distribution.Applications: Co-extrusion, blending.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.350 cc-mm/m²-24hr-atm | 0.889 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Water Vapor Transmission | 14.0 g/m²/day | 0.902 g/100 in²/day | ASTM D1434 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Secant Modulus, MD | 0.410 GPa | 59.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.460 GPa | 66.7 ksi | ASTM D882 |
| Coefficient of Friction | 0.30 | 0.30 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Overview of materials for Polyetheretherketone, Carbon Fiber Filled
- NOVA Chemicals Sclair® 8405 UV8D, 8405G UV8D MDPE Rotational Molding Resin (discontinued **)
- Karina TR-551D48/1 Black PVC Compound
- Lucite International Diakon® Frost 902 51 Acrylic Polymer
- SABIC Innovative Plastics PC0703 PC
- Sumitomo Chemical ESPOLEX® WT487X Thermoplastic Elastomer
- Teknor Apex Sarlink® 4380 Thermoplastic Elastomer
- Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Moisture)
Copyright © lookpolymers.com All Rights Reserved