- NOVA Chemicals Sclair® 11P2 Butene LLDPE Film Resin (discontinued **)
NOVA Chemicals Sclair® 11P2 Butene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11P2 Butene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Secant Modulus, MD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.230 GPa | 33.4 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 2.00 g/micron | 50.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % @Thickness 0.0250 mm |
6.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 65 % | 65 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Osprey Metals 316L/MA Master Alloy Stainless Steel Powder (Grade 90% - 16)
- SABIC Innovative Plastics Lexan® HPH4504 PPC (Asia Pacific)
- Gwent Electronic Materials P2121112P18 Nitrogen Plasma Modified Multiwalled Carbon Nanotubes
- SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copolymer (Europe-Africa-Middle East)
- Saint-Gobain Tygon® Norprene® A-60-N Drinking Water Tubing Formulation.
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- Zeon Chemicals Hydrin® C2000XL Polyepichlorohydrin Elastomer
- Dow CYCLOTENE™ XU35075 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- Ametek AM 388™ Alloy (UNS C72650) TS01
- BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved