NOVA Chemicals Sclair® 11J1 Octene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11J1 Octene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Low gel, excellent hermetic heat sealability, easy processability, high toughness and strength.Applications: Sealant web in food packaging, vacuum packaging, barrier applications, etc.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Melt Flow 0.95 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.95 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 675 %
675 %
ASTM D882
Film Elongation at Break, TD 880 %
880 %
ASTM D882
Secant Modulus, MD 0.176 GPa
25.5 ksi
ASTM D882
Secant Modulus, TD 0.200 GPa
29.0 ksi
ASTM D882
Coefficient of Friction 0.80
0.80
ASTM D1894
Elmendorf Tear Strength, MD 18.0 g/micron
457 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 24.0 g/micron
610 g/mil
ASTM D1922
Dart Drop 7.00 g/micron
178 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 41.0 MPa
5950 psi
ASTM D882
Film Tensile Strength at Break, TD 33.0 MPa
4790 psi
ASTM D882
Optical Properties Metric English Comments
Haze 10 %

@Thickness 0.0250 mm
10 %

@Thickness 0.000984 in
ASTM D1003
Gloss 58 %
58 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 220 - 230 °C
428 - 446 °F