NOVA Chemicals Novapol® TR-0735-U Hexene MDPE Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Molded
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® TR-0735-U Hexene MDPE Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Good impact resistance, Excellent processabilityApplications: Toys, Complex custom parts, Home and garden items, MailboxesAdditives: Processing antioxidants, UV stabilizersInformation provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
ASTM D792
ESCR 100% Igepal® >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
ESCR 10% Igepal® 220 hour

@Temperature 50.0 °C
220 hour

@Temperature 122 °F
F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 17.3 MPa

@Thickness 3.17 mm
2510 psi

@Thickness 0.125 in
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638
Flexural Modulus 0.780 GPa
113 ksi
1% Strain Value from rotomolded samples; ASTM D790
Impact Test 67.8 J

@Thickness 3.17 mm,
Temperature -40.0 °C
50.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
rotomolded; ARM Method
203 J

@Thickness 6.35 mm,
Temperature -40.0 °C
150 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
rotomolded; ARM Method
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 47.0 °C
117 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 37.3 °C
99.1 °F
ASTM D648