NOVA Chemicals Novapol® TR-0535-UG Hexene MDPE Rotational Molding Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Rotational Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® TR-0535-UG Hexene MDPE Rotational Molding Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Molded Plaque Properties. Features: excellent impact strength, excellent ESCR.Applications: large parts, agricultural storage tanks.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.610 g/cc | 0.0220 lb/in³ | |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition B, ASTM D1693, 100% Igepal |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 27.2 MPa | 3950 psi | ASTM D638 |
| Tensile Strength, Yield | 17.3 MPa | 2510 psi | ASTM D638 |
| Elongation at Break | 1500 % | 1500 % | ASTM D638 |
| Elongation at Yield | 17.4 % | 17.4 % | ASTM D638 |
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.20 mm |
0.993 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Tensile Impact Strength | 163 kJ/m² | 77.6 ft-lb/in² | 0.3 cm notched sample; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 128 °C | 262 °F | ASTM D3417 |
| Crystallization Temperature | 112 °C | 234 °F | ASTM D3417 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D1525 |
| Vicat Softening Point | 113 °C | 235 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 315 °C | 399 - 599 °F |