NOVA Chemicals Novapol® TF-0119-FP Hexene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® TF-0119-FP Hexene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: High strength and toughness, low gel count, intended for narrow die gaps.Applications: Stretch wrap, blend resin.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Thickness 38.1 microns
1.50 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 600 %
600 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Secant Modulus, MD 0.170 GPa
24.7 ksi
ASTM D882
Secant Modulus, TD 0.190 GPa
27.6 ksi
ASTM D882
Coefficient of Friction >= 0.60
>= 0.60
ASTM D1894
Elmendorf Tear Strength, MD 11.8 g/micron
300 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 25.5 g/micron
648 g/mil
ASTM D1922
Dart Drop 7.00 g/micron
178 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 37.0 MPa
5370 psi
ASTM D882
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ASTM D882
Optical Properties Metric English Comments
Haze 13 %

@Thickness 0.0250 mm
13 %

@Thickness 0.000984 in
ASTM D1003
Gloss 40 %
40 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 195 - 220 °C