NOVA Chemicals Novapol® PF-Y821-D Butene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® PF-Y821-D Butene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Good stiffness and machinability, good blocking resistance.Applications: Bags-on-roll, produce bags, garment film, trash bags.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D792
Thickness 38.1 microns
1.50 mil
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 550 %
550 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Secant Modulus, MD 0.200 GPa
29.0 ksi
ASTM D882
Secant Modulus, TD 0.230 GPa
33.4 ksi
ASTM D882
Coefficient of Friction <= 0.20
<= 0.20
ASTM D1894
Elmendorf Tear Strength, MD 3.30 g/micron
83.8 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 13.8 g/micron
351 g/mil
ASTM D1922
Dart Drop 3.50 g/micron
88.9 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 38.0 MPa
5510 psi
ASTM D882
Film Tensile Strength at Break, TD 27.0 MPa
3920 psi
ASTM D882
Optical Properties Metric English Comments
Haze 16 %

@Thickness 0.0250 mm
16 %

@Thickness 0.000984 in
ASTM D1003
Gloss 45 %
45 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 195 - 220 °C
383 - 428 °F