NOVA Chemicals Novapol® LF-Y320-D Fractional Melt LDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® LF-Y320-D Fractional Melt LDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: High melt strength and superior bubble stabilityEnhances throughputs in LLDPE blendsSuperior strength and toughnessExcellent shrink film characteristics Applications: Industrial packagingLinersShrink filmBlends with LLDPEInformation provided by Nova Chemicals
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D792
Thickness 38.0 microns
1.50 mil
Melt Flow 0.25 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.25 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 15.2 MPa
2200 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Yield, MD 110 %
110 %
ASTM D882
Film Elongation at Yield, TD 450 %
450 %
ASTM D882
Coefficient of Friction <= 0.20
<= 0.20
ASTM D1894
Elmendorf Tear Strength, MD 7.80 g/micron
198 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.20 g/micron
81.3 g/mil
ASTM D1922
Dart Drop 6.30 g/micron
160 g/mil
ASTM D1709/A
Film Tensile Strength at Break, MD 29.0 MPa
4200 psi
ASTM D882
Film Tensile Strength at Break, TD 23.1 MPa
3350 psi
ASTM D882
1% Secant Modulus, MD 193 MPa
28000 psi
ASTM D882
1% Secant Modulus, TD 228 MPa
33000 psi
ASTM D882
Optical Properties Metric English Comments
Haze 30 %
30 %
ASTM D1003
Gloss 20 %
20 %
at 45°; ASTM D2457