NOVA Chemicals Novapol® LF-0219-D LDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® LF-0219-D LDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Good heat sealing latitude, moderate toughness, easy processability.Applications: Liners, industrial packaging, blends with LLDPE.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D792
Thickness 38.1 microns
1.50 mil
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 34.5 MPa
5000 psi
temp
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D882
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Secant Modulus, MD 0.150 GPa
21.8 ksi
ASTM D882
Secant Modulus, TD 0.175 GPa
25.4 ksi
ASTM D882
Coefficient of Friction <= 0.20
<= 0.20
ASTM D1894
Elmendorf Tear Strength, MD 5.90 g/micron
150 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.90 g/micron
99.1 g/mil
ASTM D1922
Dart Drop 2.40 g/micron
61.0 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 18.0 MPa
2610 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Optical Properties Metric English Comments
Haze 14 %

@Thickness 0.0250 mm
14 %

@Thickness 0.000984 in
ASTM D1003
Gloss 40 %
40 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 170 - 190 °C
338 - 374 °F