NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer

Category Polymer , Thermoplastic , SMA Polymer , Styrene-Maleic Anhydride (SMA), Heat Resistant
Manufacturer NOVA Chemicals
Trade Name Dylark®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description and Features: Styrene/maleic anhydride copolymer with high-heat resistance and high modulus. Resins designed for use in foam extrusion.Processing: Contact NOVA Chemicals technical personnel for processing assistance. Data presented here is based on test results from a limited number of samples and may change as additional manufacturing data is obtained.Availability: Available in boxes, truckloads, and railcars.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D 955
Melt Flow 1.9 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.9 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8010 psi
ASTM D 638
Elongation at Break 2.2 %
2.2 %
ASTM D 638
Tensile Modulus 3.35 GPa
486 ksi
ASTM D 638
Flexural Strength 128 MPa
18600 psi
ASTM D 790
Flexural Modulus 3.66 GPa
531 ksi
ASTM D 790
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C

@Thickness 3.17 mm
244 °F

@Thickness 0.125 in
Annealed; ASTM D 648
Vicat Softening Point 131 °C

@Load 1.00 kg
268 °F

@Load 2.20 lb
Rate B; 120°C/min; ASTM D 1525